2" drain line from the main 10" line. The leakage occurred at the margin of the weld, a short time after the introduction of the reinforced ribs to reduce vibration.
642
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Field photoDf - General View
The titanium rotor blade of a flowmeter broke after two years in service in an acid environment, containing H2S.
340
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - General View
External aspect of the 8" diameter pipe that suffered localized thinning and leakage associated to the welded regions. The vertical weld is the pipe seam and the horizontal weld is the circunferential butt weld.
142
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Aspect Before AnalysisDf - Welded Joint

More from these cases

ML00179 — Hydrides in Titanium WeldM - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Low magnification micrography transverse to the fillet weld in the pipe. The pipe base metal is to the bottom of the figure and the weld metal is to the top. The heat affected zone in the middle, shows a coarse grain size structure.
60
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Welded Joint
Low magnification micrography showing the weld metal, full of pores, indicating that the field welding was not properly shileded.
50
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Weld Metal
Coarse grains in the heat affected zone.
46
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Heat Affected Zone
Micrography of the weld metal at the fillet weld where the cracking started, showing several brittle microcracks that corresponds to the regions where the fractography showed secondary crackis.
35
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Weld Metal
Micrographic detail of the weld metal brittle microcracks, in regions with hydrides formation.
32
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Weld Metal

+8 more from this case →

ML00176 — Hydride Formation in a Titanium BladeM - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Aspect by SEM of the secondary crack at the blade surface.
18
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Surface Aspect by SEMDf - At the Surface