Ferrous Alloys

1 case · 6 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Ferritic Standard: 8630 Detail focus: Weld Metal clear all

Ferrous Alloys — sub-branches

Low Alloy Steel 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite structure in the columnar (previous austenitic) grains has suffered degradation due to the long heat treatment cycle (12 hours) in high temperature.
97
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal

More from these cases

ML00129 — Non qualified WPS for High Strength SteelM - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite has suffered degradation due to the long heat treatment cycle (12 hours) in a temperature of 640°C, that is higher than the recommended for the D2 filler metal.
78
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal at the face of the joint. It is possible to see the columnar grains of acicular ferritic structure. The hardness level of this region varied a little. From 231HV10 at the root until 250HV10 close to the face.
50
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal at the face of the joint showing the acicular ferrite structure with some regions where the grains started recristalization.
49
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal at the root of the joint. It is possible to see only reheated regions of primary ferritic structure. The average hardness level of this region is 231HV10.
34
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal at the root of the joint showing the equiaxial ferritic structure.
33
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal