Low Alloy Steel

2 cases · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: ASTM Detail focus: Brittle Fracture clear all

Low Alloy Steel — sub-branches

CMn Steel 11CrMo Steel 4High Strength Low Alloy 3Low Alloy Low Carbon QT 1Low Alloy Medium Carbon QT 3Microalloyed Steel 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the fracture surface of the 2" diameter casting. The fracture appeared flat, with secondary cracks, and the position of the fracture during the loading test is located in the region that was in tensile stress during the hot dip galvanized process (the part was sustaining its own weight during the zinc hot dip bath).
801
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture
Macroscopic view of the fracture surface showing that there is a flat appearance of the fracture close to the bottom of the thread (upper side of the figure) and a flat, but rough appearance in the center of the stud. No evidences of corrosion in the thread fillets indicating that the stud was protected.
59
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture

More from these cases

ML00138 — Liquid Metal Embrittlement of a HSLA SteelM - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Scanning electron fractography in low magnification (originally 15x), showing the flat fracture surface with steps and secondary cracks.
73
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
ML00136 — Hydrogen Cracks of Subsea StudsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Fractographic aspect of the stud fracture surface, by scanning electron microscopy, close to the bottom of the thread fillet. In the center of the image it is possible to see secondary cracks with intergranular morphology.
59
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture