Low Alloy Medium Carbon QT

3 cases · 43 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Bolt clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the bolt fracture surface by scanning electron microscopy, (SEM) presenting striations that indicate a FATIGUE micromechanism. The bolt is of a medium strength (class 8.8) low alloy steel, medium carbon, quenched and tempered.
1123
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
Micrography of a longitudinal section of the bolt, as polished, presenting brittle cracks, transverse to the bolt axis.
1241
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Cracks
Multiple intergranular cracks transverse to the bolt axis. Hydrogen assisted cracking due to cathodic protection of a high strenght steel. Micrography in the "as polished" condition.
472
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Intergranular Cracking

More from these cases

ML00130 — Fatigue Fracture of Overloaded BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
The four bolts have fractured in the same position, close to the end, and the corrosion marks in the thread suggest that they have been tightened only a few fillets in a tapped hole. This condition could be responsible for overloading the fillets, relaxing the applied bolt preload, and intensifying cyclic stresses.
192
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - General View
The corrosion marks in the thread surface indicate that the bolt was not properly tightened in the tapped hole. The length of thread engagement should be at least 1x of the bolt diameter, in this case 3/8".
170
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - General View
Macroscopic aspect of the bolt fracture. Part of it is flat from the bottom of the thread.
166
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - Fracture
The head of the bolts presented the marks that indicated they were manufactured to meet ASTM A449 type 1 bolt, that is a medium strength low alloy steel, quenched and tempered.
148
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - At the Surface
Aspect of the fracture surface in low magnification, showing a flat aspect (associated to a fatigue fracture micromechanims) and a rough aspect (associated to a ductile fracture micromechanism).
167
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Fractography by SEMDf - General View

+12 more from this case →

ML00077 — Hydrogen Cracking of LAS Subsea BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Aspect of the bolt fracture. The fracture appearance is irregular and there are several secondary cracks from thread fillets.
245
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Aspect of the bolt surface with a detail of a secondary crack at the first thread fillet, close to the bolt head.
147
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Secondary Cracks
Aspect of the bolt fracture. The fracture appearance is irregular.
137
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Fracture
The longitudinal macrosection shows the fracture appearance, irregular, and a lot of secondary cracks transverse to the bolt axis, and longitudinal.
126
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Longitudinal Section AspectDf - Longitudinal Section
Several secondary cracks in the broken bolt, responsible for the irregular shape of the fracture, that presentes brittle cracks in the transverse and longitudinal directions.
109
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Longitudinal Section AspectDf - Longitudinal Section

+10 more from this case →

ML00073 — Hydrogen Cracking of a LAS Subsea FastenerM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Aspect of the fastener fracture, flat, at a thread fillet.
69
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
One side of the broken socket head screw, presenting secondary cracks in thread fillets adjacent to the position where the nut was tightened.
64
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Tempered martensitic structure of a longitudinal section of the fastener. Slightly banded material. Hardness level about 42 HRc.
59
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of a longitudinal section of the fastener, at the threat fillet, showing a transverse cracking.
68
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracking
Micrography of the secondary crack, in the fillet adjacent to the nut position, where it was opened to the surface.
65
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracking

+3 more from this case →