Super Duplex Stainless Steel

2 cases · 32 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Oil and Gas clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Fractographic detail of the longitudinal Charpy V testpiece, broken at -46°C and presenting energy of 64J (the average energy of three tespieces was 70J). The Charpy V testpiece was removed from the center of the bar. The micromechanism is quasicleavage and the test in this direction presented energy values superior than the minimum requirement of 45J.
944
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - Fractography by SEMDf - Broken Testpiece
Macrography of the pipe to flange weld. Transverse section identifying the regions of the base materials, heat affected zones and weld metal, which microstructures are presented in this ML.
527
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint

More from these cases

ML00123 — Non Qualified Superduplex for SubseaM - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Fractography of the broken Charpy V testpiece, longitudinal, broken at -46°C and presenting energy of 64J (the average of three values was 70J). In this direction the material presented an energy value higher than the minimum requirement of 45J.
109
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - Fractography by SEMDf - Broken Testpiece
Fractography of the Charpy V testpiece, transverse section, broken at -46°C and presenting energy of 20J (the average of three results was 33J). The coarse structure and the alignement created a condition for low energy results in this specific direction, and the material did not present the minimum requirement of 45J.
103
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - Fractography by SEMDf - Broken Testpiece
Micrography of a transverse section of the forged bar in the center of the thickness. Ferrite and austenite. Coarse structure.
74
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Transverse Section
Micrography of a longitudinal section of the forged bar in the center of the thickness. Ferrite and austenite. Coarse structure.
61
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Longitudinal Section
Micrography of a transverse section of the forged bar in the center of the thickness. Ferrite and austenite. The ferrite amount, measured by metallographic method, manual counting, is 59%.
53
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Transverse Section

+3 more from this case →

ML00049 — Pipe to Flange Welded Joint in a 14" ND Superduplex SpoolM - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Macrography of the pipe heat affected zone.
55
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MacroDf - Heat Affected Zone
Macrography of the flange HAZ. The macroscopic aspect shows a remarkable modified region.
56
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MacroDf - Heat Affected Zone
Micrography of the pipe base metal presenting a refined duplex ferritic austenitc structure, banded.
47
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Duplex structure
Micrographic detail of the pipe base metal presenting a refined duplex ferritic austenitc structure, banded.
55
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Base Metal
Micrographic detail of the pipe base metal presenting a refined duplex ferritic austenitc structure, banded.
56
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Duplex structure

+17 more from this case →