Precipitation Hardened Stainless Steel

2 cases · 3 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: At the Surface clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Corroded spots (shallow pits) at the spring surface.
84
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - At the Surface
Micrographic detail of the spring wire surface, far from the fracture, showing several small intergranular cracks.
40
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - At the Surface

More from these cases

ML00137 — Brittle Fracture of a 15-5 PH Valve SpringM - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
The scanning electron microscopy image presents the surface of the spring (top of the figure) where it was broken (the fracture is in the bottom of the figure). It is possible to see that there is a product at the surface and the material presents intergranular fracture, suggesting there was a hydrogen embrittlement effect. Important to observe that the material does not present pits.
58
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Fractography by SEMDf - At the Surface