Micrographic detail of the cracks in the weld metal generated from the partially melted region at the fusion line suggesting that a liquation effect propagated a solidification cracking.
18
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Hot cracking