Copper Alloy

4 cases · 48 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Alpha clear all

Copper Alloy — sub-branches

Aluminum Brass 1Aluminum Bronze 2Tin Bronze 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Visual aspect of the internal side of the tube, after longitudinal cut, presenting the region of leakage. The tube, that is 1.6mm thick, presented several points of localized diissolution .
457
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Surface AspectDf - Localized Thinning
Macrography of a ring transverse section presenting a large variation in the grain size, revealing the diferences in the solidification rate.
453
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O solution Etched MacroDf - Casting Structure
Aspect "as received" of the seamless tube at the curved position, showing the longitudinal crack and corrosion products at the tube surface.
836
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - General View
The micrography of the transverse section shows coarse grains and biphasic structure. Alpha grains and a lamellar eutectoid structure can be observed in the material.
464
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the External Surface

More from these cases

ML00170 — MIC in Aluminum Brass TubesM - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Macrography of a transverse section of the tube close to the leakage point, evidencing a localized thinning from the internal side of the tube.
65
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Localized Thinning
Visual aspect of the internal side of the tube, after longitudinal cut, presenting regions where the internal layer is fully stained.
55
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Internal Surface
Detailed aspect, by a low magnification microscope, of the internal side of the tube, after longitudinal cut. The tube, that is 1.6mm thick, presented several points of localized corrosion leading to leaks.
46
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Surface AspectDf - Localized Corrosion
Uniform granular microstructure of the aluminum brass, monophasic alpha.
44
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - FeCl3+HCl+Ethanol Etched MicroDf - Alpha
Micrographic detail of the granular structure of the aluminum brass, monophasic alpha.
44
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - FeCl3+HCl+Ethanol Etched MicroDf - Alpha

+10 more from this case →

ML00166 — Tin Bronze Wear Ring of Seawater PumpM - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Low magnification micrography of a transverse section of the ring showing a dendritic structure.
64
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrography of a transverse section of the ring showing a cored alpha structure with segregation at interdendritic regions. This structure is in a region close to the ring surface.
52
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrography of a transverse section of the ring showing a cored alpha structure with strong segregation at interdendritic regions, and regions of a white structure at grain boundaries. This structure is in a region close to the center of the ring.
51
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrographic detail of the cored alpha structure with light segregation at intergranular regions (light layer at grain boundaries), and a white euctetoid structure (alpha and delta) at interdendritic space. This structure is in a region close to the ring surface, where the solidification was quicker.
49
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Grain boundary intermetallics
Micrographic detail of the cored alpha structure with strong segregation at intergranular regions (dark layer at grain boundaries), and a white euctetoid structure (alpha and delta) at interdendritic space. This structure is in a region close to the center of the ring, where the solidification was slower.
47
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Grain boundary intermetallics

+2 more from this case →

ML00165 — SCC of Aluminum Bronze Heating CoilM - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Aspect of the external tube surface after cleaning. It is possible to see that the cracks are longitudinal to the tube and localized in positions where the surface is corroded.
132
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Surface AspectDf - External Surface
Aspect of the internal tube surface after a longitudinal cut, without cleaning. It is possible to see a clean surface inside the tube.
104
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Surface AspectDf - Internal Surface
Micrography of the tranverse section of the tube, in the center of the thickness. There are small grains and large grains, characterizing a dual grain size. The large grains size is about 100 microns, more than 10 times larger than the average size of the smaller grains size.
101
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Dual grain sizes
Micrographic detail of the alpha microstructure presenting dual grain sizes. Two different types of twins are presented in the structure: annealing twins and deformation twins, suggesting that the material was probably partially recristalized after cold deformation and stress relief treatment.
87
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Alpha
Micrography of a transverse section of the bent tube, external surface (OD) to the top and internal surface (ID) to the bottom of the figure. At the through wall cracking position, the external surface presented a layer of intergranular corrosion.
95
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - As polished micrographyDf - Cracking

+12 more from this case →

ML00044 — Centrifugally Cast CuAl BushingM - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Micrographic detail of the structure at the external surface.
58
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the External Surface
The micrography of the transverse section shows coarse grains and biphasic structure. No diferentes close to the internal surface. Alpha grains and a lamellar eutectoid structure can be observed in the material.
46
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the Internal Surface
Micrographic detail of the structure at the internal surface.
38
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the Internal Surface
Detail of the structure in the center of the thickness. Alpha grains and lamellar eutectoid structure.
28
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - In the Center of the Thickness
The macrography of the transverse section shows the columnar grains typical of a centrifugally cast material. The etch is the same as the adopted for the micrographies. The bushing thickness is 1/2".
41
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - Transverse Section AspectDf - Columnar Grains