Copper Alloy

4 cases · 20 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Used Capture method: Optical Microscope clear all

Copper Alloy — sub-branches

Aluminum Bronze 1Brass 1Cupronickel 1Tin Bronze 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification micrography of a transverse section of the ring showing a dendritic structure.
64
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Metallographic aspect of the polished surface of the (back of the) coaster, showing pores and shrinkages, typical of a casting structure.
49
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - As polished micrographyDf - Casting Structure
The micrography of the transverse section shows coarse grains and biphasic structure. Alpha grains and a lamellar eutectoid structure can be observed in the material.
464
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the External Surface
The micrography of the tube shows a granular structure and light deformation lines. No evidences of corrosion from the external surface (upper side of the figure) or internal surface (lower side of the figure).
440
VIEW
ML00043 / Apr.2017
CuNi Condenser Tube
M - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Longitudinal Section

More from these cases

ML00166 — Tin Bronze Wear Ring of Seawater PumpM - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Micrography of a transverse section of the ring showing a cored alpha structure with segregation at interdendritic regions. This structure is in a region close to the ring surface.
52
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrography of a transverse section of the ring showing a cored alpha structure with strong segregation at interdendritic regions, and regions of a white structure at grain boundaries. This structure is in a region close to the center of the ring.
51
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrographic detail of the cored alpha structure with light segregation at intergranular regions (light layer at grain boundaries), and a white euctetoid structure (alpha and delta) at interdendritic space. This structure is in a region close to the ring surface, where the solidification was quicker.
49
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Grain boundary intermetallics
Micrographic detail of the cored alpha structure with strong segregation at intergranular regions (dark layer at grain boundaries), and a white euctetoid structure (alpha and delta) at interdendritic space. This structure is in a region close to the center of the ring, where the solidification was slower.
47
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Grain boundary intermetallics
Tin Bronze Wear Ring of Seawater Pump
2
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - General View

+1 more from this case →

ML00156 — Antique Silver Plated Decorative PieceM - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Same region of the previous image but is a higher magnification, showing the metallographic aspect of the polished surface of the (back of the) coaster. Shrinkage with a dendritic morphology typical of a casting structure.
48
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - As polished micrographyDf - Voids
Low magnification metallography of the coaster after etching, revealing a casting structure of alpha plus beta phases. Beta is the dark brown matrix phase and alpha is the dendritic yellow phase.
45
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Alpha and Beta
Metallography of the coaster after etching, revealing a casting structure of alpha plus beta phases. Beta is the dark brown matrix phase and alpha is the dendritic yellow phase.
48
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Alpha and Beta
High magnification metallography of the coaster after etching, revealing a casting structure of alpha plus beta phases. Beta is the dark brown matrix phase and alpha is the dendritic yellow phase. The non destructive preparation created a metallographic surface not well polished (full of grinding scratches).
48
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Alpha and Beta
ML00044 — Centrifugally Cast CuAl BushingM - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Micrographic detail of the structure at the external surface.
58
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the External Surface
The micrography of the transverse section shows coarse grains and biphasic structure. No diferentes close to the internal surface. Alpha grains and a lamellar eutectoid structure can be observed in the material.
46
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the Internal Surface
Micrographic detail of the structure at the internal surface.
38
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the Internal Surface
Detail of the structure in the center of the thickness. Alpha grains and lamellar eutectoid structure.
28
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - In the Center of the Thickness
ML00043 — CuNi Condenser TubeM - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
The material structure is monophasic.
110
VIEW
ML00043 / Apr.2017
CuNi Condenser Tube
M - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Single phase
Detail of the structure at the surface.
79
VIEW
ML00043 / Apr.2017
CuNi Condenser Tube
M - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - At the Surface