Copper Alloy

3 cases · 30 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Ship Capture method: Optical Microscope clear all

Copper Alloy — sub-branches

Aluminum Bronze 1Brass 1Tin Bronze 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification micrography of a transverse section of the ring showing a dendritic structure.
64
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrography of the tranverse section of the tube, in the center of the thickness. There are small grains and large grains, characterizing a dual grain size. The large grains size is about 100 microns, more than 10 times larger than the average size of the smaller grains size.
101
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Dual grain sizes
Micrography of a transverse section of the platesheet presenting a duplex structure, alpha (light yellow) and beta (orange) phases.
214
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - FeCl3+HCl+Ethanol Etched MicroDf - Alpha and Beta

More from these cases

ML00166 — Tin Bronze Wear Ring of Seawater PumpM - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Micrography of a transverse section of the ring showing a cored alpha structure with segregation at interdendritic regions. This structure is in a region close to the ring surface.
52
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrography of a transverse section of the ring showing a cored alpha structure with strong segregation at interdendritic regions, and regions of a white structure at grain boundaries. This structure is in a region close to the center of the ring.
51
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrographic detail of the cored alpha structure with light segregation at intergranular regions (light layer at grain boundaries), and a white euctetoid structure (alpha and delta) at interdendritic space. This structure is in a region close to the ring surface, where the solidification was quicker.
49
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Grain boundary intermetallics
Micrographic detail of the cored alpha structure with strong segregation at intergranular regions (dark layer at grain boundaries), and a white euctetoid structure (alpha and delta) at interdendritic space. This structure is in a region close to the center of the ring, where the solidification was slower.
47
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Grain boundary intermetallics
Tin Bronze Wear Ring of Seawater Pump
2
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - General View

+1 more from this case →

ML00165 — SCC of Aluminum Bronze Heating CoilM - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Micrographic detail of the alpha microstructure presenting dual grain sizes. Two different types of twins are presented in the structure: annealing twins and deformation twins, suggesting that the material was probably partially recristalized after cold deformation and stress relief treatment.
87
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Alpha
Micrography of a transverse section of the bent tube, external surface (OD) to the top and internal surface (ID) to the bottom of the figure. At the through wall cracking position, the external surface presented a layer of intergranular corrosion.
95
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - As polished micrographyDf - Cracking
Micrographic detail of the external side of the bent tube, as polished, showing detachement of several grains due to the intergranular corrosion layer. The corroded layer is about 200 microns thick at this position.
89
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - As polished micrographyDf - Intergranular Corrosion
Micrographic detail of the external side of the tube, showing the layer of intergranular corrosion and the through ewall integranular stress corrosion cracking.
88
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - As polished micrographyDf - Through Wall Cracking
Micrography of the external side of the bent tube, showing detachement of several grains due to intergranular corrosion. The corroded layer is about 200 microns thick at this position. The differences of colours in the corroded layer suggests a dealloying effect, also known as selective leaching.
71
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - External Surface

+4 more from this case →

ML00125 — Dezincification of a Cooler TubesheetM - BrassP - PlateAp - ShipCd - Preferential Dissolution
Micrography of the transverse section of the platesheet at the interface between the corroded and the non-corroded regions. The micrography is in the as polished condition.
140
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Preferential Dissolution
Micrography of the transverse section of the platesheet showing that part of the material (right side in the top of the figure) was lost (corroded).
129
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Preferential Dissolution
Micrographic detail of the dezincification effect, where the beta phase is preferentially corroded, leaving a cooper rich phase (red) that is porous and easily cracks.
121
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Dezincification
Micrographic detail of the dezincification effect, where the beta phase is preferentially corroded, leaving a cooper rich phase (red) that is porous and easily cracks.
130
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Cracks
Micrography showing detachment of material at the surface of the platesheet. The cracks are associated to the dezincification effect, where the beta phase was preferentially corroded and became a weak porous layer.
113
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Crack

+7 more from this case →