Hot cracking

1 case · 1 image

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Search & filters

Search

1 image

TryML00175 corrosion ML00083 brittle fracture ductile behavior fatigue hydrogen fracture embrittlement stress corrosion

Browse by category (6)

Material3

Ferrous Alloys1 case
Heat Resistant Steel1 case
High Alloy Steel1 case

Product2

Cast Ftitting1 case
Finished Product1 case

Condition3

Damage1 case
Repair Defect1 case
Welding1 case

Microstructure3

Austenitic Matrix1 case
Network of Primary Carbides1 case
Secondary carbides1 case

Standard7

2971 case
A1 case
ASTM1 case
grade HP1 case
Modified1 case
N087051 case
UNS1 case

Capture method2

Kalling Etched Micrography by OM1 image
Optical Microscope1 image

Atlas / Detail focus / Welding Defect / Hot cracking

Application: Petrochemical ×clear all

Results

SortNewest Oldest Title A-Z Title Z-A

Micrographic detail of the cracks in the weld metal generated from the partially melted region at the fusion line suggesting that a liquation effect propagated a solidification cracking.

18

ML00173 / May.2021

Welding Cracks in an Aged HP Cast Fitting

M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding

Cm - Kalling Etched Micrography by OMDf - Hot cracking