Casting Structure

4 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of a ring transverse section presenting a large variation in the grain size, revealing the diferences in the solidification rate.
453
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O solution Etched MacroDf - Casting Structure
Metallographic aspect of the polished surface of the (back of the) coaster, showing pores and shrinkages, typical of a casting structure.
49
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - As polished micrographyDf - Casting Structure
The macrography of a transverse section of the new tube shows that there are shrinkage voids close to the internal surface, that is exposed to high temperature air. The tube is a 4" diameter and 1/4" thick.
62
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Transverse Section AspectDf - Casting Structure
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
419
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure

More from these cases

ML00097 — Cast SS Tube Removed From High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
The macrography of a transverse section of the tube removed from service after 6 months, with damage close to the internal tube surface. The tube is a 4" diameter and 1/4" thick.
41
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Transverse Section AspectDf - Casting Structure
ML00058 — High-Pressure Piston Seal in Casting Al AlloyM - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
45
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
34
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure
Micrography of the cast Aluminum alloy (AlSnCuNi) typically adopted for bearing applications.
32
VIEW
ML00058 / Apr.2017
High-Pressure Piston Seal in Casting Al Alloy
M - Aluminum TinP - CastingAp - EnergyCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Casting Structure