Multiple cracks

3 cases · 3 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: UNS Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the cracks at the fusion line, associated to the partially melted region suggesting a liquation effect in a material that presented low ductility. After opening the cracks they propagate brittle into the base metal and created a solidification cracking in the weld metal, detailed in the next figures.
23
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Multiple cracks
Micrography of a longitudinal section of the spring, at the surface, indicating that there are multiple intergranular cracks initiating from the pit.
26
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Multiple cracks
Micrography of the stub end longitudinal section, presenting multiple cracks, branched.
40
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - As polished micrographyDf - Multiple cracks