Microstructure

9 cases · 41 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Granular Capture method: Optical Microscope clear all

Microstructure — sub-branches

Aligned particles 2Austenite 10Bainite 1Clad Interface 10Columnar Grains 1Duplex structure 1Equiaxial Grains 1Ferrite 3Grain refined structure 1Granular structure 6Non Metallic Inclusions 2Strain Hardened 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the fork handle in the center of the transverse section, curved, presenting larger ferritic grains with elongated morphology.
70
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Micro by OM, HCl + Ethanol + Picric AcidDf - Granular structure
Micrography of the plate in a section, in the middle of the thickness. The aligned pitting is associated to the chemical etch of inclusions and second phases. The structure is granular but the grain boundaries do not appear at that magnification, originally 50x.
50
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched Micrography by OMDf - Aligned particles
Micrographic detail of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
61
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Image by scanning electron microscopy of the metallurgically bonded interface of the internally cladded pipe. It is a longitudinal seam welded pipe, with substrate in low alloy steel X65 and clad plate in Alloy 625 (welded by a solid state process). The region is a detail in the side of the Ni alloy clad plate where a grain refinement has occurred probably due to recrystallization of a strain hardened region during later heat treatment. The microhardness of this region is a lot higher than the value obtained out of this region, in the clad plate.
904
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Oxalic Acid Electrolytic EtchDf - Clad Interface
Micrographic detail of the austenitic structure at the surface, where the grain size of the material increased. By optical microscopy the intragranular precipitation due to solution annealing and aging is not revealed.
794
VIEW
ML00089 / Sep.2017
Inconel 718 Allen Bolt for Subsea Application
M - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
Micrography of the nut in the longitudinal direction, at the Nylon insert position, showing a cold formed region at the end of the nut, with high hardness levels (about 600 HV100g).
53
VIEW
ML00062 / Apr.2017
Inconel 718 Lock Nut with Polymer Insert
M - NiCrFe AlloyP - Cold FormedAp - PipingCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Strain Hardened
Granular austenitic structure close to the surface of the shaft.
61
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - Austenite
The microstructure of the pipe base metal, in the center of the thickness, is granular alpha.
102
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Granular structure

More from these cases

ML00151 — Ferritic Stainless Steel of a Flatware ForkM - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Micrographic detail of the ferritic grains with elongated morphology in the center of the transverse section, curved.
58
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Micro by OM, HCl + Ethanol + Picric AcidDf - Ferrite
The micrography as polished in the transverse section shows a small amount of inclusions in the steel.
62
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - As polished micrographyDf - Non Metallic Inclusions
Detail of the non metallic inclusions in the steel. The yellow and black colours and morphologies suggest Ti base and oxides.
65
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - As polished micrographyDf - Non Metallic Inclusions
Micrography of a fork longitudinal section, in the center of the thickness, at the scoop position. The ferritic grains are equiaxial and uniform.
49
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Micro by OM, HCl + Ethanol + Picric AcidDf - Granular structure
Micrography of a fork handle in the longitudinal section, presenting the larger ferritic grains.
45
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Micro by OM, HCl + Ethanol + Picric AcidDf - Granular structure

+2 more from this case →

ML00145 — Impact of a .380 Winchester on 6061 T6 PlateM - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Micrography of the plate in a section, in the middle of the thickness, in a position where the plate was not affected by the shot. The microstructure is granular although the grain boundaries are not resolvable at this magnification. The black spots are localized corrosion in aligned particles.
49
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched Micrography by OMDf - Aligned particles
Micrographic detail of the plate in the middle of the thickness. At this magnification it is possible to see the grain boundaries and the black spots are localized etching in aligned particles.
43
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched Micrography by OMDf - Granular structure
Micrographic detail of the plate in the middle of the thickness. At this magnification it is possible to see the grain boundaries and the black spots are localized etching in aligned particles.
37
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched Micrography by OMDf - Granular structure
Micrography of the damaged plate at the side of the bullet impact, top of the figure. The perforated hole expulsed the material to the top and bottom directions. There are evidences of plastic deformation of the plate microstructure and the hardness level close to the hole increased from 123 HV to 131 HV (1kg)
17
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched Micrography by OMDf - Strain Hardened
ML00135 — MIC of a Non Magnetic Drilling ToolM - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Micrographic detail of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked.
59
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
ML00133 — Seam Welded Pipe Cladded with Alloy 625M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Micrographic detail of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure,
50
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the pipe at the interface with the clad plate, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
55
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrography of a longitudinal section of the pipe at the interface with the clad plate, with Nital etch that reveals only the low alloy steel structure, to the left side of the image.
51
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrographic detail of a longitudinal section of the pipe at the interface with the clad plate, with Nital etch that reveals only the low alloy steel structure, to the left side of the image. The metallurgical bonding of the claded plate to the substrate is evident since there are no voids or defects.
47
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrography showing the positions of Vickers microhardness measurements in the longitudinal micrography, in the pipe steel substrate (dot 1 - 266 HV100g), very close to the interface inside the clad plate (dot 2 - 429 HV100g) and a little far from the interface inside the Ni clad plate (dot 3 - 358 HV100g).
50
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Clad Interface

+8 more from this case →

ML00089 — Inconel 718 Allen Bolt for Subsea ApplicationM - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
The micrography of a longitudinal section of the bolt, in the center of the thickness (ND 1/2"), shows an equiaxial granular structure. Although the material was hardened by heat treatment (solution annealing and aging), the microstructure at this magnification does not reveal the intragranular precipitation.
34
VIEW
ML00089 / Sep.2017
Inconel 718 Allen Bolt for Subsea Application
M - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Equiaxial Grains
Micrographic detail of a longitudinal section of the bolt, close to the surface (ND 1/2"). The grain size is higher than the center of the bolt.
27
VIEW
ML00089 / Sep.2017
Inconel 718 Allen Bolt for Subsea Application
M - NiCrFe AlloyP - Machined PartAp - SubseaCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Austenite
ML00062 — Inconel 718 Lock Nut with Polymer InsertM - NiCrFe AlloyP - Cold FormedAp - PipingCd - Typical manufacturing
Micrographic detail of the nut at the cold formed region where the nut was bent over the Nylon insert. It is possible to see strain hardened structures (600HV 100g).
41
VIEW
ML00062 / Apr.2017
Inconel 718 Lock Nut with Polymer Insert
M - NiCrFe AlloyP - Cold FormedAp - PipingCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Strain Hardened
ML00041 — Fatigue Fracture of Inconel 718 Spline ShaftM - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Duplex grain size structure, austenitic. The small grains are probably due to the arresting effect of the delta phase during fabrication in high temperature.
47
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Kalling Etched Micrography by OMDf - Duplex structure
ML00005 — Environmental Hydrogen Damage in Ti PipeM - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
The microstructure of the pipe seam weld metal, in the center of the thickness, presents a coarse prior beta grain size.
85
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Columnar Grains