Carburized Layer

2 cases · 5 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Bainite clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the longitudinal section of the tube, close to the external surface. The carburizing layer consists of a bainitic structure, with intergranular and intragranular carbide precipitation.
1184
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Carburized Layer
Micrography of a longitudinal section of the pin, at the surface. The pin was carburized, quenched and tempered (yellow diffuse layer at the surface, 0.5 mm of extension) and a white layer of hard chromium plating is evident.
108
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Carburized Layer

More from these cases

ML00107 — Carburized 9Cr1MoV Superheater TubeM - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Micrography of the longitudinal section of the tube, close to the external surface. A scale is evident at the surface as well as a carburizing layer.
549
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Carburized Layer
ML00081 — Hydrogen Cracking of a Chromium Plated Carburized PinM - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Macrography of the longitudinal section of the 2" diameter pin close to the fracture surface (top of the figure) in a section where the pin presented the final fracture (it is deformed). The lubrication hole is in the right side of the figure. It is possible to see several secondary cracks at the surface of the pin (left side of the figure), propagating only where there is a carburized layer. It is possible to see that the end of each secondary crack is blunted.
67
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - NItal Etched MacroDf - Carburized Layer
Micrography that presents a secondary cracking (adjacent to the broken surface) propagating 500 microns from the surface, where there is a white layer of hard chromium .
78
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Carburized Layer