Intergranular Cracking

5 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: As polished micrography clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic aspect of the multiple intergranular cracks, initiating from the bottom of a pit.
25
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Intergranular Cracking
SAMPLE 1, AT THE FRACTURE - Micrographic detail, as polished, of the oxides that are penetrating in the austenitic grain boundaries. The oxidation created intergranular cracks in regions close to the edge of the rectangular tube, that are more susceptible to suffer cyclic thermal stresses, since the furnace is weekly turned off, during two days.
55
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - Intergranular Cracking
Micrography of a longitudinal section of the bolt, in a position close to the fracture (top) and bolt surface (left ), presenting several secondary intergranular cracks.
57
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Intergranular Cracking
Micrography of a longitudinal section of the spring indicating that under the deposits there are intergranular cracks initiating at the spring surface.
72
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - As polished micrographyDf - Intergranular Cracking
Micrographic detail of a transverse section of the ring, showing the corroded martensitic structure (chemical dissolution) inside the pitting.
33
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - As polished micrographyDf - Intergranular Cracking

More from these cases

ML00172 — Brittle Fracture of a LAS Valve SpringM - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Micrographic detail of the intergranular cracks, initiating from the bottom of a pit.
29
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Intergranular Cracking
ML00139 — Hydrogen Fracture of a 17-4 PH Allen BoltM - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of the secondary intergranular cracks close to the surface of the bolt, where the fracture occurred.
56
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Intergranular Cracking
ML00137 — Brittle Fracture of a 15-5 PH Valve SpringM - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Micrographic detail of a longitudinal section of the spring indicating that under the deposits there are intergranular cracks initiating at the spring surface.
65
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - As polished micrographyDf - Intergranular Cracking