The intergranular morphology of the cracks, at the heat affected zone of the forging, indicates it is a cold cracking probably formed when the welded joint was not yet post welding heat treated. The actual hardness values at the HAZ is 270HV10, and when it was cracked it was probably a lot higher.
71
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Intergranular Cracking
Micrography of a longitudinal section of the bolt, in a position close to the fracture (top) and bolt surface (left ), presenting several secondary intergranular cracks.
57
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Intergranular Cracking
The fractography by SEM shows intergranular fracture close to the external surface of the pin.
93
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Cracking
Fractographic analysis of the pin showing a region of predominantly intergranular fracture micromechanism.
46
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Surface Aspect by SEMDf - Intergranular Cracking

More from these cases

ML00178 — Cold cracks in Cr-Mo Welded ForgingM - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Detail of the cold cracking at the previous austenite grain boundary of the martensitic structure.
55
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Intergranular Cracking
Detail of the cold cracking at the previous austenite grain boundary of the martensitic structure.
59
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Intergranular Cracking
ML00139 — Hydrogen Fracture of a 17-4 PH Allen BoltM - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of the secondary intergranular cracks close to the surface of the bolt, where the fracture occurred.
56
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Intergranular Cracking
Micrographic detail of the intergranular cracks in the transition between the threaded body and the head of the non broken bolt, indicating that this bolt was also embrittled and could fail soon.
48
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
ML00009 — Hydrogen Cracking of a 5" Drill Pipe S135M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Fractographic detail by SEM of the intergranular fracture close to the external surface of the pin.
83
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Cracking
Micrography of a longitudinal section of the pin, at the fracture position, showing the main fracture surface and secondary cracks associated to a segregation band, with an intergranular morphology.
49
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
ML00088 — Hydrogen Cracking of an API 5D S135 Drill PipeM - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of a secondary intergranular cracking at the pin longitudinal section (transverse to the fracture).
38
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking