Damage

4 cases · 35 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Longitudinal Seam Welded Pipe clear all

Damage — sub-branches

Brittle Cracks 1Corrosion 1Crack 1Cracking 1Fatigue Crack 1Fatigue Striation 2Fracture 2Hydride Formation 3Leakage 3Localized Corrosion 6Localized Thinning 5Margin of the Weld Crack 1Microcracks 2Preferential Dissolution 5Through Wall Cracking 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of a transverse section of the 4" pipe showing the barnacles adhered to the internal pipe surface, and the leakage position (in the top of the figure). It is possible to see that the deposits are attached all throught the internal pipe perimeter but the damage is localized. The damage morphology suggests it is a crack, or a welding defect, but the microstructural analysis indicated that the damage is a galvanic effect at the autogenous seam weld.
1135
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Longitudinal Section AspectDf - Localized Corrosion
Micrography of the welded joint fusion line presenting the liquation cracking. The weld metal is in the right side (bottom) and the forged connector heat affected zone is in the left side (top).
83
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracking
The main pipe, ND 18", has suffered a pipe through wall cracking at the margin of the 1 1/2" branch socket weld.
664
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Crack
Internal aspect of the 8" diameter pipe that suffered localized thinning and leakage. The vertical weld is the pipe seam and the horizontal weld is the circunferential butt weld.
564
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Aspect Before AnalysisDf - Localized Thinning

More from these cases

ML00140 — Preferential Corrosion of Pipe Seam WeldM - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Detail of the transverse section of the 4" pipe at the longitudinal seam weld evidencing the leakage position. The damage appears as a through wall opening. The pipe thickness is 8 mm and there are no evidences of general corrosion (the SCH 80 corresponds to 8.6 mm) or pitting at the internal surface.
99
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Leakage
Aspect of the internal surface of the pipe after cutting, showing the colors of the internal deposits and the leaking line associated to the pipe seam.
288
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Leakage
Detailed aspect of the internal surface of the pipe after cleaning, in a region where the pipe was leaking.
62
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Leakage
Detail of the transverse section of the 4" pipe at the longitudinal seam weld where it is not leaking yet, showing that the damage is not a crack but a localized dissolution, or localized corrosion or preferential dissolution at the autogenous seam weld. The thickness of the pipe is 8 mm and there are no evidences of general corrosion or pitting.
63
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Localized Corrosion
Macrography of a transverse section of the pipe, 8 mm thick, presenting localized dissolution at the longitudinal autogenous seam weld.
65
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - NItal Etched MacroDf - Preferential Dissolution

+9 more from this case →

ML00072 — Liquation Cracks in a High Strength JointM - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
The HAZ presents microcracks at previous austenite grain boundaries. These regions melted during welding and generated cracks associated to low melting temperature phases.
48
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Microcracks
The HAZ presents microcracks at previous austenite grain boundaries. These regions melted during welding and generated cracks associated to low melting temperature phases.
43
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Microcracks
ML00006 — Vibration Induced Fatigue in 304SSM - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
The macro section transverse to the welded region, show that the through wall cracking occurred in the pipe base metal, from the margin of the weld.
191
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Through Wall Cracking
Macro transverse to the weld showing that the fracture occurred in the main pipe, at the margin of the weld.
163
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Fracture
The fracture surface of the main pipe is presented in low magnification (external pipe surface in the top) showing a flat propagation starting from the contour of the weld margin.
173
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Margin of the Weld Crack
Fracture surface micromechanism by striation, evidence of FATIGUE.
158
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation
Fracture surface micromechanism by striation, evidence of FATIGUE.
147
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation

+2 more from this case →

ML00005 — Environmental Hydrogen Damage in Ti PipeM - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Aspect of the internal surface of the pipe at the welded region, showing the interface of the thinning area in the weld and the pipe base metal.
128
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Surface Aspect by SEMDf - Localized Thinning
Region of the localized thinning at the weld metal, in a metallographic section, as polished. In the base metal the hydride layer is continuous and no thinning is evident (left side of the figure) and in the weld metal it is detached and cracked (right side of the figure).
107
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Micrography by SEMDf - Localized Thinning
The pipe base metal, at the internal surface, presents a hydride layer showing that the environment is absorbing hydrogen. Although there are microcracks in this layer it did not detach in the base metal.
102
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Hydride Formation
The pipe internal suface, at the welded region, presents no hydride layer (because it has detached) as well as the material itself is suffering brittle detachment.
71
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Localized Thinning
Detail, as polished, of brittle cracks in the weld metal, from the internal side of the pipe.
67
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Micrography by OMDf - Brittle Cracks

+3 more from this case →