Damage

3 cases · 19 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Fitting clear all

Damage — sub-branches

Branched Cracks 3Brittle Fracture 4Cleavage Facets 1Corrosion Cracking 1Crack 2Fracture 3Intergranular Fracture 1Microcracks 1Through Wall Cracking 1Transgranular Cracking 1Transgranular Fracture 1

Results

SortNewestOldestTitle A-ZTitle Z-A
The hose connector fracture surface presented different fracture micromechanisms associated to the microstructure: inclusion decohesion, small regions of intergranular fractures (probably due to cementite at grain boundaries), and cleavage of the ferritic structure. All these mechanisms are brittle.
560
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Fractography by SEMDf - Brittle Fracture
Detail, by scanning electron microscopy, of the external surface of the line at the cracking position presenting branched cracks, transverse to the line axis. The surface of the fitting is fully stained (dark grey), from where the cracks start, indicating that the material loose passivation in these regions.
62
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Branched Cracks
Micrographic detail of the region where the cracking was initiated at the internal side of the fitting.
41
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - NaOH Electrolytic Etched MicroDf - Through Wall Cracking

More from these cases

ML00103 — Brittle Fracture of a Free-Cutting ConnectorM - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Aspect of the internal side of the connector. The fracture, in the longitudinal direction, presents a brittle aspect. The thickness of the connector is about 2 mm.
126
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Brittle Fracture
Macroscopic detail of the brittle fracture, in the longitudinal direction.
105
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Brittle Fracture
Details of the inclusion decohesion and cleavage.
89
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Fractography by SEMDf - Cleavage Facets
Details of the cleavage fracture in the ferritic structure.
86
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Fractography by SEMDf - Brittle Fracture
Details of the intergranular fracture, probably associated to cementite at grain boundaries.
68
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Fractography by SEMDf - Intergranular Fracture

+6 more from this case →

ML00095 — MIC of a Riser Control LineM - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Micrography of the longitudinal section of the hydraulic line sample at the cracking position, localized in the fitting and starting from the outer diameter (OD).
48
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Micrography by OM using A262 Method ADf - Branched Cracks
Micrographic detail of the branched cracks at the fitting, close to OD.
40
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Micrography by OM using A262 Method ADf - Branched Cracks
Detail of one region that had the passivation layer destroyed and presented corrosion cracks.
48
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Corrosion Cracking
The aspect of the external surface of the fitting shows regions where the passivation was lost and where microcracks started already.
54
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Microcracks
ML00094 — MIC of a Subsea Hydraulic LineM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
The through wall cracking was opened by citting the two sides and the aspect was characterized by SEM. Although there was a film at the fracture surface, probably because the fitting was removed from service some time after it was leaking, the fracture micromechanism is by quasecleavage, typical of a stress corrosion cracking.
56
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Fractography by SEMDf - Transgranular Fracture