Damage

3 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Creep clear all

Damage — sub-branches

Crack 1Cracks 1Interconnected Cracks 1Oxide Layer 1Through Wall Cracking 2Voids 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the cracking after Dye Check Test (Liquid Penetrant) in the external side of the line that operates at 800°C, insulated, and presented the leakage associated to the longitudinal seam weld of the fitting. The circumferential butt weld of the fitting to a pipe did not fail. See the schematic drawing in the next figure
371
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Aspect by NDTDf - Through Wall Cracking
Micrography, in the as polished condition, of the TUBE REMOVED FROM SERVICE, centrifugally cast, in the transverse section, presenting external surface oxides and voids.
35
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Voids
Micrography of a longitudinal section of the bolt at the fracture surface. The material showed several creep voids and interconnected cracks. The broken bolt remained in service during some time and the fracture surface presented a thick oxide layer(grey). As polished.
529
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Micrography by OMDf - Oxide Layer

More from these cases

ML00061 — Creep in a Seam Weld of a 304H SS FittingM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Schematic drawing presenting the aspect of the cracking after Dye Check Test (Liquid Penetrant) in the external side of the line that operates at 800°C, insulated, and presented the leakage associated to the longitudinal seam weld of the fitting. The circumferential butt weld of the fitting to a pipe did not fail.
62
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Identification drawingDf - Through Wall Cracking
Through wall cracking in the longitudinal seam weld of the fitting. Several cracks, longitudinal to the weld, were created by the connection of voids in the weld metal, associated to a strong microstructural evolution.
191
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Cracks
ML00004 — Creep in High Temperature BoltsM - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Micrographic detail of the creep voids and interconnected cracks. The broken bolt remained in service during some time and the fracture surface presented a thick oxide layer(grey). As polished.
121
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Micrography by OMDf - Interconnected Cracks
Micrographic detail of the creep voids and interconnected cracks. The broken bolt remained in service during some time and the fracture surface presented a thick oxide layer(grey). As polished.
101
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Micrography by OMDf - Voids
Micrography of a longitudinal section of a CrMov steel bolt that broke in service by a creep mechanism in a gas turbine. Tempered structure. Interconnected cracks paralled to the fracture surface.
95
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Nital Etched Micrography by OMDf - Crack