Damage

3 cases · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Monophasic Capture method: Optical Microscope clear all

Damage — sub-branches

Cracks 1Localized Corrosion 1Localized Thinning 1Thinning 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic aspect, as polished, of a transverse section of the tube (bottom side of the image, orange), at the interface between the tube and the melted steel over the external diameter (top side of the image, grey). In the copper tube there are several microcracks and regions of incipient melting (voids).
41
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - As polished micrographyDf - Cracks
Micrography of a transverse section of the tube, close to the leakage point. The thickness is localized reduced where the internal passive layer was ruptured, and the chemical effect of the biological proliferation created a high corrosion rate.
26
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - FeCl3+HCl+Ethanol Etched MicroDf - Localized Thinning
Detail of the leakage region, at the weld metal/fuson line near the elbow.
96
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Kalling Etched Micrography by OMDf - Thinning

More from these cases

ML00170 — MIC in Aluminum Brass TubesM - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
MIC in Aluminum Brass Tubes
2
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - FeCl3+HCl+Ethanol Etched MicroDf - Localized Corrosion