Damage

1 case · 10 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Brittle Behavior Microstructure: Zinc Layer Capture method: Optical Microscope clear all

Damage — sub-branches

Cracking 2Cracks 2Fracture 1Intergranular Cracking 1Secondary Cracks 4

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the section transverse to the fracture (top of the figure). The fracture is intergranular, there are several secondary cracks, and there are deposits of zinc over the fracture. The zinc makes difficult the etch with Nital to reveal the microstructure close to the fracture surface.
67
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Fracture

More from these cases

ML00138 — Liquid Metal Embrittlement of a HSLA SteelM - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Micrography of the cracking parallel to the fracture, as polished. The fracture is branched, there are several secondary cracks, with a clear intergranular morphology.
65
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - As polished micrographyDf - Cracking
Micrographic detail of the branch cracking parallel to the fracture, as polished, showing that the cracks are filled with zinc.
62
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - As polished micrographyDf - Secondary Cracks
Micrography of the branch cracking parallel to the fracture. There are several secondary intergranular cracks and the cracks are filled with zinc. The zinc appears dark because of the Nital etch, and the steel is not fully revealed because of the protection by the zinc.
54
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracking
Micrographic detail of the secondary intergranular cracks, filled with zinc. The zinc appears dark because of the Nital etch, and the steel is not fully revealed because of the protection by the zinc.
48
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks
Micrography of the branch cracking parallel to the fracture. There are several secondary intergranular cracks and the cracks are filled with zinc. The zinc appears dark because of the Nital etch, and the steel close to the cracking is not fully revealed because of the protection by the zinc.
41
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracks

+4 more from this case →