Damage

1 case · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Petrochemical clear all

Damage — sub-branches

Aged Microstructure 2Cracks 4Multiple cracks 1

Results

SortNewestOldestTitle A-ZTitle Z-A
After removal of the cracked part of the fitting, the dye check test indicated the presence of several cracks in the internal diameter (ID), out of the buttered layer, that means, in the fitting base metal.
42
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Aspect by NDTDf - Cracks

More from these cases

ML00173 — Welding Cracks in an Aged HP Cast FittingM - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cast fitting microstructure. The material presented a network of primary carbided and an austenitic matrix with coalescing secondary precipitation.
37
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Aged Microstructure
Micrographic detail of the network of primary carbided, white and grey, and an austenitic matrix with coalescing secondary precipitation.
30
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Aged Microstructure
Macrographic detail close to the internal diameter (ID in the bottom), where the cracks were detected by dye check (after removal of the damaged part of the cast fitting). Close to the surface it is possible to see the layers of the weld metal that corresponds to the cast fitting buttering.
21
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched MacroDf - Cracks
Micrographic detail of the cracks at the fusion line, associated to the partially melted region suggesting a liquation effect in a material that presented low ductility. After opening the cracks they propagate brittle into the base metal and created a solidification cracking in the weld metal, detailed in the next figures.
23
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Multiple cracks
Micrographic detail of the cracks in the base metal created from the partially melted region suggesting that a liquation effect propagated brittle cracks into the low ductility base metal.
30
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Cracks

+1 more from this case →