Damage

2 cases · 11 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Energy Standard: AISI Capture method: Optical Microscope clear all

Damage — sub-branches

Corrosion 2Crack 4Cracks 1Intergranular Cracking 4

Results

SortNewestOldestTitle A-ZTitle Z-A
Detailed microstructure of the plate base metal, exposed to high temperature exhausting gases. Refined austenite, precipitation of carbides in the grain boumdaries and some cracks.
24
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Crack
Micrography of a transverse section of the ring, at the pitting position, as polished, showing that there are intergranular cracks and the martensitic structure is corroded (chemical dissolution) inside the pitting.
33
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - As polished micrographyDf - Corrosion

More from these cases

ML00174 — Carburization of a 347 SS Welded JointM - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Detailed microstructure of the weld metal, exposed to high temperature exhausting gases. Austeno-ferritic structure, strong carbide precipitation integranular and transgranular, and some cracks.
23
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Cracks
Detailed microstructure of the heat affected zone, fully carburized and cracked intergranular. Large austenitic grain size.
20
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Intergranular Cracking
ML00124 — MIC of a Martensitic Valve RingM - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Micrographic detail of a transverse section of the ring, showing the corroded martensitic structure (chemical dissolution) inside the pitting.
32
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - As polished micrographyDf - Corrosion
Micrographic detail of a transverse section of the ring, showing the corroded martensitic structure (chemical dissolution) inside the pitting.
33
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - As polished micrographyDf - Intergranular Cracking
Micrography of a transverse section of the ring at the cracking position. The cracks are intergranular and opened at the position close to the surface. it is possible to identify dissolution of the structure adjacent to the grain boundaries,
25
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Crack
Micrographic detail of a transverse section of the ring at the cracking position. The cracks are intergranular and opened at the position close to the surface. it is possible to identify dissolution of the structure adjacent to the grain boundaries,
24
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
Micrograph showing a fine acicular martensitic matrix with a branching crack network, more extensive near the right edge.
25
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Crack

+2 more from this case →