Fatigue Striation

1 case · 1 image

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Search & filters

Search

1 image

TryML00037 corrosion ML00025 brittle fracture ductile behavior fatigue hydrogen fracture embrittlement stress corrosion

Browse by category (6)

Capture method2

Fracture Surface Aspect1 image
Naked Eye or Stereoscope1 image

Microstructure28

Tempered Martensite10 cases
Austenite9 cases
Ferritic Bainitic5 cases
Ferritic pearlitic5 cases
Bainite4 cases
Duplex Ferritic Austenitic4 cases
Martensite4 cases
Aged Martensite3 cases

+20 more

Dendritic3 cases
Granular3 cases
Segregation Bands3 cases
Strain Hardened3 cases
Alpha2 cases
Austeno ferritic2 cases
Coarse Structure2 cases
Pearlitic2 cases
Precipitation Hardened2 cases
Refined ferritic2 cases
Small Amount of Delta Phase2 cases
Acicular Ferrite1 case
Anisotropy1 case
Coating Layer1 case
Degradated1 case
Detrimental phases1 case
Ferritic1 case
Heterogeneous granulometry1 case
Pearlite Highly Strained1 case
Zinc Layer1 case

Standard74

UNS23 cases
ASTM13 cases
A12 cases
AISI9 cases
ALLOY6 cases
5375 cases
API5 cases
Class 15 cases

+66 more

and 26 more not shown here — refine in the Atlas

Product33

Finished Product24 cases
Raw Material20 cases
Welded Joint7 cases
Rolled Plate5 cases
Bolt4 cases
Forging4 cases
Pipe4 cases
Cladding3 cases

+25 more

Fabrication Weld3 cases
Fastener3 cases
Spring3 cases
Bar2 cases
Longitudinal Seam Welded Pipe2 cases
Seamless Pipe2 cases
Shaft2 cases
Wire Rope2 cases
Allen Stud1 case
Blade1 case
Case1 case
Casting1 case
Fitting1 case
Machined Part1 case
Nut1 case
Piping spool1 case
Pressure Vessel1 case
Seamless tube1 case
Stud1 case
Tool1 case
Tube1 case
Tubular Forging1 case
Valve Body1 case
Welded Testpiece for Qualification1 case
Wire1 case

Condition26

Damage25 cases
Sound10 cases
Corrosion8 cases
Hydrogen8 cases
Hydrogen Embrittlement7 cases
Typical manufacturing7 cases
Fabrication Defect4 cases
Brittle Behavior3 cases

+18 more

Brittle Behavior3 cases
Brittle Fracture3 cases
Welding3 cases
Removed From Service2 cases
Stress Corrosion2 cases
Used2 cases
Corrosion Fatigue1 case
Crevice1 case
Fatigue1 case
Heat Treatment Defect1 case
Hydride Formation1 case
Localized Dissolution1 case
Non qualified1 case
Not according to spec1 case
Vibration Induced Fatigue1 case
Wear1 case
Welding Defect1 case
WPS1 case

Material26

Ferrous Alloys31 cases
Low Alloy Steel16 cases
High Alloy Steel10 cases
Low Alloy Medium Carbon QT8 cases
CMn Steel5 cases
Non Ferrous Alloys5 cases
Carbon Steel4 cases
Austenitic Stainless Steel3 cases

+18 more

Nickel Alloy3 cases
NiCrFe Alloy3 cases
Precipitation Hardened Stainless Steel3 cases
Combinations2 cases
High Carbon Steel2 cases
LAS / Ni Alloy2 cases
Martensitic Stainless Steel2 cases
Super Duplex Stainless Steel2 cases
Aluminum Bronze1 case
Copper Alloy1 case
High Strength Low Alloy1 case
Low Carbon Steel1 case
Medium Carbon Steel1 case
Medium Carbon Tool Steel1 case
Microalloyed Steel1 case
Titanium Alloy1 case
Tool Steel1 case
Unalloyed Titanium1 case

Atlas / Detail focus / Damage / Fatigue Striation

Application: Oil and Gas ×clear all

Results

SortNewest Oldest Title A-Z Title Z-A

The propagation of the crack is also transgranular, without plastic deformation, by fatigue.

26

ML00176 / Nov.2021

Hydride Formation in a Titanium Blade

M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation

Cm - Fracture Surface AspectDf - Fatigue Striation

© copyright. All rights reserved
Version 1.0