Ductile Fracture

7 cases · 13 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: UNS clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
WHEEL 1 fracture detail showing a small shrinkage in the left side of the photo and dimples in the right side of the photo.
73
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Fractography by SEMDf - Ductile Fracture
Macrography of one wire that was overloaded, showing localized necking and large plastic deformation close to the fracture. This kind of fracture occurred for about 25% of the broken wires.
50
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Ductile Fracture
Detail of the margin of the perforated hole in the impact position. It is interesting to observe extreme plastic deformation created by the perforation expulsing the material from the hole, in the direction of the impact.
28
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface Aspect by SEMDf - Ductile Fracture
Detailed aspect of the eye bolt fracture position, with strong plastic deformation indicating ductile overloading. The red marks in the thread surface of the bolt (in the left side of the image) correspond to the position where the nut was tight. Thread fillets adjacent to the fracture presented secondary cracks.
1125
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Aspect Before AnalysisDf - Ductile Fracture
Micrographic detail of the pin in a longitudinal section, transverse to the fracture surface, at the ductile final fracture, presenting microvoids connecting with plastic deformation of the structure.
41
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Ductile Fracture
Microscopic aspect of the fracture, close to the bolt surface where the fracture is macroscopically ductile (probably the final fracture), presenting dimples as the fracture micromechanism.
89
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Ductile Fracture
The fracture surface is ductile and the micromechanism is dimples, elongated due to the shearing action.
83
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - Fractography by SEMDf - Ductile Fracture

More from these cases

ML00183 — Ductile Behavior of an Aluminum WheelM - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
WHEEL 1 fracture detail showing predominantly dimples as the fracture micromechanism.
74
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Fracture Surface AspectDf - Ductile Fracture
Low magnification view of the broken tensile specimen fracture surface. The same macroscopic aspect as the WHEEL 1 fracture surface.
48
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Testpiece aspectDf - Ductile Fracture
ML00155 — Failure of a Prestressed Concrete Steel StrandM - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Micrography of a typical overloaded wire, in a longitudinal section, showing plastic deformation and necking at the fracture. About 25% of the wires have ruptured by this ductile mechanism.
34
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Ductile Fracture
Micrography of a typical as polished overloaded wire, in a longitudinal section, showing necking at the fracture and secondary ductile cracks. About 25% of the wires have ruptured by this ductile mechanism.
35
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polished micrographyDf - Ductile Fracture
ML00145 — Impact of a .380 Winchester on 6061 T6 PlateM - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Margin of the perforated hole showing regions of fracture and a striated appearance at the plate surface (right side of the figure). This aspect is associated to the plate manufacturing.
14
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Fractography by SEMDf - Ductile Fracture
Micrography of the damaged plate close to the perforated hole, in the middle of the thickness, showing the strong plastic deformation of the structure and ductile secondary cracks.
10
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched Micrography by OMDf - Ductile Fracture