Cracks

5 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Scanning Electron Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
WHEEL 1 fracture detail showing small regions with smooth aspect, and brittle microcracks. But predominantly the micromechanism is by dimples.
70
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Fractography by SEMDf - Cracks
Microscopic aspect of the cracks at the tooth surface. The cracks are flat and propagating longitudinally to the tooth (and secondary short transverse).
45
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Surface Aspect by SEMDf - Cracks
Micrography of the bottom of the thread fillet, presenting secondary cracks of intergranular morphology, propagating transverse to the stud axis, but presenting longitudinal openings.
27
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by SEMDf - Cracks
The microscopic aspect of the internal side of the housing evidences the characteristics of the multiple cracks, not directly related to pitting corrosion.
41
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Cracks
Hot cracks in the fusion zone. The eutectic regions were melted and cracked in an interdendritic morphology.
37
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Cracks

More from these cases

ML00183 — Ductile Behavior of an Aluminum WheelM - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
WHEEL 1 fracture detail of the brittle microcracks. The analysis of the material microstructure showed that these microcracks are associated to iron rich phases.
68
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Fractography by SEMDf - Cracks
Detail of the micrography transverse to the fracture surface of the WHEEL 1, close to the void, that is a region of impurities. The iron rich particles are brittle and with several microcracks, that did not propagate during the impact.
27
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Micrography by SEMDf - Cracks
ML00070 — Automotive Light Alloy Wheel Repaired By WeldingM - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Detail of the hot cracks in the fusion zone. The eutectic regions were melted and cracked in an interdendritic morphology. Keller etch.
50
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Cracks