Cracking

4 cases · 6 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Tempered Martensite Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
As polished micrography of the bottom of the thread fillet, where a cracking is still closed, showing the microscopical morphology of the cracking.
40
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracking
Micrographic detail of the secondary crack, paralel to fracture, at the internal diameter of the padeye. The microstructure is martensitic.
14
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Cracking
Micrography of a longitudinal section of the fastener, at the threat fillet, showing a transverse cracking.
68
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracking
Micrography of the welded joint fusion line presenting the liquation cracking. The weld metal is in the right side (bottom) and the forged connector heat affected zone is in the left side (top).
83
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracking

More from these cases

ML00073 — Hydrogen Cracking of a LAS Subsea FastenerM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Micrography of the secondary crack, in the fillet adjacent to the nut position, where it was opened to the surface.
65
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracking
Micrographic detail of the secondary crack, in the fillet adjacent to the nut position, where it was opened to the surface.
46
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracking