Used

2 cases · 19 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Casting Capture method: Scanning Electron Microscope clear all

Used — sub-branches

Removed From Service 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification micrography of the welded region, showing the interface between the base in the bottom and the fusion zone (between the liquidus and solidus temperatures), as well as the weld metal in the top. There are pores close to the weld metal and in the fusion zone the interdendritic space was melted and the eutectic morphology was changed. Keller etch.
50
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Weld Repair
Micrographic detail of the original casting blade structure. The tempered martensite is more clearly revealed by the scanning electron microscopy. The average hardness level measured in this side is 270 HV.
70
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Left Side

More from these cases

ML00070 — Automotive Light Alloy Wheel Repaired By WeldingM - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Micrographic detail of the cast rim at the heat affected zone presenting coalesced Si particles at the interdendritic space an neddles of Fe rich phase. Keller etch.
47
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Heat Affected Zone
The coalesced silicon particles in the interdendritic space of the base metal presents a remelting at the fusion zone. The micrography by SEM shows the exactly line where the eutectic is remelted and refined. Keller etch.
40
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Fusion Line
Refined dendrites in the weld metal. The Si/Al alpha eutectic in the interdendritic space is also refined. Keller etch.
38
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Weld Metal
Hot cracks in the fusion zone. The eutectic regions were melted and cracked in an interdendritic morphology.
37
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Cracks
Detail of the hot cracks in the fusion zone. The eutectic regions were melted and cracked in an interdendritic morphology. Keller etch.
50
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by SEMDf - Cracks
ML00055 — CA6NM Blade Remanufactured by WeldingM - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Higher magnification of the martensitic structure of the original casting blade structure, hardness level of 270HV10.
26
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Left Side
Micrographic detail of the inserted casting structure. The martensite presents a less tempering aspect than the original casting revealing that it was heat treated in a different condition. The average hardness level measured in this side is 370 HV.
157
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Right Side
Higher magnification of the martensitic structure of the inserted casting structure, hardness level of 370HV10.
23
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Base Metal Right Side
Micrographic detail of the original casting blade fusion line, presenting the tempered martensitic structure similar for the HAZ (left side of the figure) and the weld metal (right side of the figure).
20
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Fusion Line Left Side
Micrographic detail of the original casting blade fusion line, presenting the tempered martensitic structure similar for the HAZ (left side of the figure) and the weld metal (right side of the figure).
20
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Fusion Line Left Side

+7 more from this case →