Used

3 cases · 17 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Ferritic pearlitic Standard: UNS Capture method: Optical Microscope clear all

Used — sub-branches

Removed From Service 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a transverse section of the engine bearing, close to the internal surface, showing two layers of bearing alloys that presents a total thickness of 600 microns.
29
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Surface Layer
Micrography of the longitudinal section of the shaft, in the center of the thickness, presenting a ferritic-perlitic structure typical of a hot forming process.
149
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of a longitudinal section of the pipe showing that the carbon steel pipe is slightly banded and there is a decarburized layer at the solid solution welded interface. The stainless steel structure (in the right side of the figure) is not revealed using the Nital etch.
126
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section

More from these cases

ML00083 — Steel Back of a Bimetallic Engine BearingM - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Micrographic detail of a transverse section of the back steel of an engine bearing, presenting a predominantly ferritic structure, strain hardened.
26
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of a transverse section of the back steel of an engine bearing, presenting a predominantly ferritic structure, strain hardened.
24
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Strain Hardened
Micrography of a transverse section of the back steel of an engine bearing, presenting a predominantly ferritic structure, strain hardened.
24
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Strain Hardened
ML00064 — SAE 1045 Steel ShaftM - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Micrographic detail of the ferritic-perlitic structure, typical of a hot forming process, in the center of the thickness.
139
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrographic detail of the ferritic-perlitic structure, typical of a hot forming process, in the center of the thickness.
116
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of the longitudinal section of the shaft, at the damaged surface (with a light wear). In low magnification the ferritic perlitic texture reveals the forging lines.
102
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrographic detail of the ferritic-perlitic structure at the surface where the wear damage is light.
92
VIEW
ML00064 / Apr.2017
SAE 1045 Steel Shaft
M - Medium Carbon SteelP - ShaftAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - At the Surface
ML00056 — Seamless Tube Externally Cladded with SSM - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Micrography of a longitudinal section of the pipe showing the carbon steel pipe , internal.
123
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a longitudinal section of the pipe showing the stainless steel pipe , external.
100
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrographic detail of the interface in the longitudinal section of the pipe showing the Vickers (300g) microhardness values, close to the interface in the carbon steel side and in the stainless steel side. Although the Nital etch does not allow to reveal the structure in the stainless steel side, the high hardness values show that the structure is different.
113
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of the interface in the longitudinal section of the pipe showing the decarburized layer at the solid solution welded interface. The stainless steel structure (in the right side of the figure) is not revealed using the Nital etch.
80
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrography of the interface between the carbon steel that is strongly etched by the electrolytic oxalic acid (in the left side of the figure) and the stainless steel, in the longitudinal section of the pipe. There is a strain hardened layer very close to the interface, at the stainless steel side.
79
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Longitudinal Section

+2 more from this case →