Aspect of the wheel. See the schematic drawing in the next figure
467
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View
Detail of the longitudinal section of the ring, showing a fully ferritic structure.
619
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section

More from these cases

ML00070 — Automotive Light Alloy Wheel Repaired By WeldingM - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Schematic drawing presenting the position in the rim where the repair by welding was conducted. The region was machined after the welding.
77
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Identification drawingDf - Weld Repair
Profile of the rim of the wheel, total width 215 mm. See the schematic drawing in the next figure.
64
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Transverse Section AspectDf - Transverse Section
Schematic drawing indicating the location of the repair by welding
60
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Identification drawingDf - Transverse Section
Detail of the welded region in the rim of the light alloy wheel.
126
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Aspect Before AnalysisDf - At the Surface
Aspect of the welded region after dye check showing several indications, later identified as hot cracks associated to the repair welding.
114
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Aspect by NDTDf - Cracks

+14 more from this case →

ML00057 — Low Carbon Steel of Segment RingM - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Longitudinal section of the ring, showing a fully ferritic structure.
128
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
The longitudinal section of the ring reveals a very fine ferritic structure.
115
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Transverse section of the ring presenting a fully ferritic structure, that presents a hardness level a little higher probably due to a cold forming effect.
93
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Transverse Section
Transverse section of the ring presenting a fully ferritic structure, that presents a hardness level a little higher probably due to a cold forming effect.
54
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Transverse Section