Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the weld metal with islands of a coarse ferritic structure, degradated (recristalized) from an acicular morphology during to the long heat treatment cycle in high temperature. The post welding heat treatment (PWHT) was conducted during 12 hours at 640°C.
700
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Coarse Structure
Micrography of the welded joint, at the root, presenting hot cracks. The imposed high energy in the root due to the ceramic backing support created a condition for cracking.
1100
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Hot cracking

More from these cases

ML00129 — Non qualified WPS for High Strength SteelM - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite structure in the columnar (previous austenitic) grains has suffered degradation due to the long heat treatment cycle (12 hours) in high temperature.
97
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite has suffered degradation due to the long heat treatment cycle (12 hours) in a temperature of 640°C, that is higher than the recommended for the D2 filler metal.
78
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the base metal, in low magnification, showing regions of segregations in a quenched and tempered martensitic structure.
52
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of the base metal showing a quenched and tempered martensitic structure. The base metal adopted in the test coupon presented a hardness level of 217HB (Brinell hardness of the certificate) and after the PWHT cycle the measured base metal hardness is 224 HV10.
59
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the base metal structure, quenched and tempered martensite. The base metal adopted in the test coupon presented a hardness level of 217HB (Brinell hardness of the certificate) and after the PWHT cycle the measured base metal hardness is 224 HV10.
51
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Martensite

+12 more from this case →

ML00118 — Non qualified GMAW of Aluminum PlatesM - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Micrography of the welded joint, at the root, showing hot cracks with intergranular morphology.
146
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Hot cracking
Micrographic detail of the welded joint, at the root, presenting hot cracks. The presence of these defects were responsible for reducing the material strenght (rupturing in lower strenght than the requirements) and ductility (cracking in bending tests).
116
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Hot cracking
Low magnification micrography of the plate base metal, presenting granular structure not clearly identified and aligned particles.
88
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Base Metal
Micrography of the plate base metal, presenting granular structure evidenced by the different shadows in the grains.
76
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Base Metal
Micrographic detail of the aligned particles in the plate base metal. The grain boundaries are not clearly identified in this higher magnification.
73
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Keller Etched Micrography by OMDf - Base Metal

+6 more from this case →