Hydrogen

2 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Oil and Gas Microstructure: Aged Martensite Capture method: Scanning Electron Microscope clear all

Hydrogen — sub-branches

Hydrogen Embrittlement 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Fractographic aspect of the broken fastener, at the surface, showing na intergranular morphology typical of a hydrogen assisted mechanism of a high strenght steel under cathodic protection.
224
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Cracking
The spring presents intergranular and transgranular brittle aspects in the fracture surface.
886
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture

More from these cases

ML00074 — Hydrogen Cracking of a 17-4 PH Subsea BoltM - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Microscopic aspect of the fracture, close to the bolt surface where the fracture is macroscopically brittle, presenting a predominantly intergranular fracture micromechanism.
108
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
Microscopic aspect of the fracture, in the center of the bolt, presenting partial intergranular fracture micromechanism and partial quase cleavage mechanism.
98
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
Microscopic aspect of the fracture, close to the bolt surface where the fracture is macroscopically ductile (probably the final fracture), presenting dimples as the fracture micromechanism.
89
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Ductile Fracture
ML00076 — Hydrogen Cracking of a 17-7 PH Subsea SpringM - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
The low magnification fractography by SEM shows a brittle fracture of the spring wire, with several secondary cracks.
45
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
The fractography by SEM presents intergranular (in the previous austenite grain boundaries) and transgranular fracture micromechanisms. Several secondary cracks perpendicular to the fracture surface.
46
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture