High Temperature

3 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Transverse Section Aspect clear all

High Temperature — sub-branches

Carburization 2Creep 3Microstructural Evolution 1Overheating 1Scaling 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Transverse section of the tube in a position of localized thinning.
60
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Transverse Section AspectDf - Localized Thinning
Transverse section macrography of the plate where the degradation by thinning is worst, close to the original corners of the tube. The thinning is occurrring from the product reaction side (side A to the bottom of the figure). The macrography shows a reduction in the thickness from 2 mm (right side, sample 2) to almost zero (left side, sample 1).
86
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Transverse Section AspectDf - Thinning
The macrography of a transverse section of the new tube shows that there are shrinkage voids close to the internal surface, that is exposed to high temperature air. The tube is a 4" diameter and 1/4" thick.
62
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Transverse Section AspectDf - Casting Structure

More from these cases

ML00180 — Local Melting of Copper Cooling TubesM - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Transverse section of the tube in a position of wall perforation.
32
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Transverse Section AspectDf - Leakage
Local Melting of Copper Cooling Tubes
1
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Transverse Section AspectDf - Thinning
Local Melting of Copper Cooling Tubes
1
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Transverse Section AspectDf - Leakage
ML00097 — Cast SS Tube Removed From High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
The macrography of a transverse section of the tube removed from service after 6 months, with damage close to the internal tube surface. The tube is a 4" diameter and 1/4" thick.
41
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Transverse Section AspectDf - Casting Structure