Damage

3 cases · 16 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Coarse Structure Detail focus: Sampling and Analysis clear all

Damage — sub-branches

Fabrication Defect 1High Temperature 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the 3 1/2" diameter tube after the water leakage in high temperature.
963
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Aspect Before AnalysisDf - General View
The carcass was manufactured using niobium stabilized plates, grade AISI 347, with circumferential welds, where the through wall cracks were detected.
301
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Field photoDf - General View
Fractographic detail of the longitudinal Charpy V testpiece, broken at -46°C and presenting energy of 64J (the average energy of three tespieces was 70J). The Charpy V testpiece was removed from the center of the bar. The micromechanism is quasicleavage and the test in this direction presented energy values superior than the minimum requirement of 45J.
944
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - Fractography by SEMDf - Broken Testpiece

More from these cases

ML00180 — Local Melting of Copper Cooling TubesM - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
View of the iinternal side of the tube (water side), deformed in the overheated area. There are several leaking points.
115
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Aspect Before AnalysisDf - Internal Surface
Macroscopic aspect after cutting longitudinally in two halfs, at the damaged area. The tube internal surface showed a red copper colour at the overheated region and the perforation is associated to longitudinal cracks.
104
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Longitudinal Section AspectDf - Internal Surface
Micrographic aspect of the tube out of the damaged region, in a longitudinal section, showing the grain refined copper structure.
96
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - FeCl3+HCl+H2O Etched MicroDf - In the Center of the Thickness
ML00174 — Carburization of a 347 SS Welded JointM - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Aspect of one region where the cracks appeared, after grinding and polishing. Several branched cracks located in welded regions. It is the region where the sample was taken.
37
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Aspect Before AnalysisDf - At the Surface
Sample surface. Microstructure of the plate base metal, exposed to high temperature exhausting gases. Refined austenite and some cracks.
24
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Base Metal
Sample surface. Microstructure of the weld metal, exposed to high temperature exhausting gases. Austeno-ferritic structure and some cracks.
20
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Weld Metal
Sample surface. Microstructure of the heat affected zone (weld metal to the left side and base metal to the right side), exposed to high temperature exhausting gases. Large austenitic grain size and cracks fully opened and filled with oxides.
24
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Heat Affected Zone
ML00123 — Non Qualified Superduplex for SubseaM - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Fractography of the broken Charpy V testpiece, longitudinal, broken at -46°C and presenting energy of 64J (the average of three values was 70J). In this direction the material presented an energy value higher than the minimum requirement of 45J.
109
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - Fractography by SEMDf - Broken Testpiece
Fractography of the Charpy V testpiece, transverse section, broken at -46°C and presenting energy of 20J (the average of three results was 33J). The coarse structure and the alignement created a condition for low energy results in this specific direction, and the material did not present the minimum requirement of 45J.
103
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - Fractography by SEMDf - Broken Testpiece
Micrography of a transverse section of the forged bar in the center of the thickness. Ferrite and austenite. Coarse structure.
74
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Transverse Section
Micrography of a longitudinal section of the forged bar in the center of the thickness. Ferrite and austenite. Coarse structure.
61
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Longitudinal Section
Micrography of a transverse section of the forged bar in the center of the thickness. Ferrite and austenite. The ferrite amount, measured by metallographic method, manual counting, is 59%.
53
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Transverse Section

+1 more from this case →