Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Tempered Martensite Standard: API Capture method: Scanning Electron Microscope clear all

Damage — sub-branches

Corrosion 2Ductile Behavior 1Fabrication Defect 2Hydrogen 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Fractographic analysis of the pin fracture surface showing inter and transgranular morphologies of fracture micromechanisms.
53
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture

More from these cases

ML00088 — Hydrogen Cracking of an API 5D S135 Drill PipeM - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Fractographic analysis of the pin showing several secondary intergranular cracks (in the middle of the figure) and quasecleavage transgranular fracture mechanism.
45
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Surface Aspect by SEMDf - Brittle Fracture
Fractographic analysis of the pin detailing a region of predominantly quasecleavage fracture micromechanism, associated to a macroscopic flat fracture surface.
46
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Surface Aspect by SEMDf - Cleavage Facets
Fractographic analysis of the pin showing a region of predominantly intergranular fracture micromechanism.
46
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Surface Aspect by SEMDf - Intergranular Cracking