Damage

19 cases · 42 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Austenite Capture method: Aspect Before Analysis clear all

Damage — sub-branches

Corrosion 12Fatigue 5High Temperature 5Hydrogen 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the equipment presenting a through wall cracking at the margin of the fillet weld.
142
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - Cracking
Aspect of the hydraulic line samples removed from service to be analyzed. Tubing and welded joint (bottom sample) between the 316 tubing (left side of the sample) and the nitronic fitting (right side of the sample). The cracking is located 10 mm far from the weld, autogenous orbital GTAW.
108
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - General View
General view of the 2" branch line that was supporting an instrument in a 12" gas piping of an offshore unity. The branch line is composed by a seamless pipe welded to a weldolet (left side of the figure) and to a flange (right side of the figure). The leakage is associated to a through wall cracking in the middle of the pipe length. The cracking is not evidenced in the figure, since it is too thin. See the schematic drawing in the next figure
494
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Brittle aspect of the failure of the conector in the male thread. Both sides of the fracture.
96
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Macroscopic aspect of the stud that broke transverse to the axis, at the bottom of the thread fillet, presenting a brittle aspect.
64
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Aspect of the heat exchanger plate showing the rupture of the plate in multiple cracks, starting at the side of the crude oil with high salinity.
727
VIEW
ML00051 / Apr.2020
Chloride SCC of 316 Heat Exchanger Plate
M - Austenitic Stainless SteelP - Heat Exchanger PartAp - FPSOCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - Cracking
Macroscopic aspect of the 1" shaft fracture surface, revealing beach marks at the surface typical of fatigue, initiated from the surface of the spline shaft at the gear position.
498
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
Visual aspect of the 3/8" diameter pin surface, presenting several lozalized corrosion spots.
53
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - At the Surface

More from these cases

ML00095 — MIC of a Riser Control LineM - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Detail of the welded joint between the 316 tubing (left side) and the nitronic fitting (right side). The through wall cracking is transverse to the line, in the fitting, 10 mm far from the weld, where the fitting was slightly bent to be assembled (cold bent).
65
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Welded Joint
ML00012 — Vibration Induced Fatigue in a 316/316L SSM - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Aspect of the internal surface of the pipe after longitudinal cutting, presenting a straight cracking, circumferential. The weldolet is to the left side and the flange is to the right side. See the schematic drawing in the next figure.
89
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
Aspect of the internal surface of the 2" nominal diameter pipe, SCH 40, presenting a circumferential through wall cracking in the pipe, not associated to any of the welded joints. It is possible to see the cracking parallel to the two welded joints: the pipe to weldolet (left side of the figure); and the pipe to flange (right side of the figure).
64
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Through Wall Cracking
Aspect of the internal surface of the 2" nominal diameter pipe, SCH 40, presenting a circumferential through wall cracking in the pipe, not associated to any of the welded joints. It is possible to see the cracking parallel to the two welded joints: the pipe to weldolet (left side of the figure); and the pipe to flange (right side of the figure).
57
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Through Wall Cracking
Circumferential cracking in the middle of the pipe, view from the external side. Several pits close to the cracking.
57
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - External Surface
ML00041 — Fatigue Fracture of Inconel 718 Spline ShaftM - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
xx
117
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - At the Surface
Macroscopic aspect of the 1" shaft fracture surface, revealing beach marks at the surface typical of fatigue, initiated from the surface of the spline shaft at the gear position.
121
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture