Damage

2 cases · 2 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Carburized Layer Capture method: Aspect Before Analysis Detail focus: Damage clear all

Damage — sub-branches

High Temperature 1Hydrogen 1Wear 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Wear of a Carburized Hypoid Gear
1
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Aspect Before AnalysisDf - Cracks
The aspect of the pin fracture surface shows that a fatigue crack propagated from the pin surface at the edge of a lubrication hole in the chromium plated pin.
83
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Fatigue Fracture