Damage

1 case · 3 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Subsea Microstructure: Coating Layer Capture method: As polished micrography clear all

Damage — sub-branches

Hydrogen 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the longitudinal section of the bolt at the bottom of the thread fillet, in the "as polished" condition, showing the zinc flakes coating layer, applied by a painting process that do not create metallurgical bonding with the substrate.
82
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Coating Layer

More from these cases

ML00126 — Hydrogen Fracture of Subsea Allen BoltsM - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of the zinc flakes coating layer in the "as polished" condition of a longitudinal section of the bolt.
71
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Coating Layer
Micrography of the longitudinal section of the bolt, at the fracture (top of the figure), starting from the bottom of the thread (to the left side of the figure). The presence of the coating at the bolt surface shows that the fracture occurred without corrosion. The rusted aspect of the fracture is associated to corrosion products after the rupture has occurred, also suggesting that the bolts were fractured and remained in service for some time after the failure occurred.
65
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Fracture