Damage

5 cases · 12 images for “fracture”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Structure clear all

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
General aspect of the degradated wires of the strand, most part presenting rust and rupture. There are two mais aspects of the degradation: wire thickness reduction by corrosion and cracks creating a longitudinal fracture of several wires.
96
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Detail of the margin of the perforated hole in the impact position. It is interesting to observe extreme plastic deformation created by the perforation expulsing the material from the hole, in the direction of the impact.
28
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Surface Aspect by SEMDf - Ductile Fracture
Margin of the perforated hole showing regions of fracture and a smooth appearance in the hole surface (right side of the figure). This smooth aspect was generated by the film of melted material from the bullet.
44
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Fractography by SEMDf - Ductile Fracture
Aspect of the all weld metal broken tensile test conducted in the sample removed from structure close to the region where the cracking was detected, indicating that the material entrapped hydrogen for several days, since the test was conducted more than 2 weeks later than the cracking was detected.
61
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Fracture Surface AspectDf - Fish Eye
The fracture surface is flat and smashed due to the shearing action.
87
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - Aspect Before AnalysisDf - Fracture

More from these cases

ML00155 — Failure of a Prestressed Concrete Steel StrandM - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Macrography of one wire that was overloaded, showing localized necking and large plastic deformation close to the fracture. This kind of fracture occurred for about 25% of the broken wires.
50
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Ductile Fracture
Micrography of a typical overloaded wire, in a longitudinal section, showing plastic deformation and necking at the fracture. About 25% of the wires have ruptured by this ductile mechanism.
34
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Ductile Fracture
Micrography of a typical as polished overloaded wire, in a longitudinal section, showing necking at the fracture and secondary ductile cracks. About 25% of the wires have ruptured by this ductile mechanism.
35
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polished micrographyDf - Ductile Fracture
Failure of a Prestressed Concrete Steel Strand
2
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
ML00145 — Impact of a .380 Winchester on 6061 T6 PlateM - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Margin of the perforated hole showing regions of fracture and a striated appearance at the plate surface (right side of the figure). This aspect is associated to the plate manufacturing.
14
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Fractography by SEMDf - Ductile Fracture
Micrography of the damaged plate close to the perforated hole, in the middle of the thickness, showing the strong plastic deformation of the structure and ductile secondary cracks.
10
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Keller Etched Micrography by OMDf - Ductile Fracture
ML00007 — Free Machining Brass in Shear PinM - BrassP - Machined PartAp - LiftingCd - Shear
The fracture surface is ductile and the micromechanism is dimples, elongated due to the shearing action.
83
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - Fractography by SEMDf - Ductile Fracture