Damage

3 cases · 20 images for “corrosion”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Ship Detail focus: Sampling and Analysis clear all

Damage — sub-branches

Corrosion 3

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Aspect before cleaning of the heavy U bolt pipe clamp, 38 mm diameter wire, at the fractured position. It is possible to see that it broke in a region where the clamp was no longer coated and there is no insert in the groove (at the internal clamp diameter). The fracture is transverse to the clamp axis.
522
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Micrography of the pipe transverse section presenting a granular microstructure.
147
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by OMDf - Transverse Section
Aspect "as received" of the seamless tube at the curved position, showing the longitudinal crack and corrosion products at the tube surface.
836
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Aspect of the U bolt clamp with partial detachment of the coating (white brown) in a region where the polimeric insert (dirty white) is still in the wire groove at the internal clamp diameter (ID).
91
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - General View
Metallographic image of a longitudinal section of the clamp (axis in the vertical direction), showing a refined ferritic perlitic structure.
34
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
The clamp presented several cracks, parallel, transverse to the axis. The appearance of the cracks in the metallographic section shows that some cracks propagate and growth with a irregular path.
24
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
ML00140 — Preferential Corrosion of Pipe Seam WeldM - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Aspect of the 4" pipe that was in seawater service for 8 years and leaked in a longitudinal line that corresponds to the seam weld. The internal surface presented thick deposits. Although the pipe was cut with a thermal process, the analysis was conducted after mechanical cutting.
100
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - General View
Detail of the transverse section of the 4" pipe 90° from the seam weld. The thickness of the pipe is 8 mm. No evidences of general corrosion or pitting were identified.
77
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Transverse Section
Detail of the transverse section of the 4" pipe 90° from the seam weld. The thickness of the pipe is 8 mm. No evidences of general corrosion or pitting were identified.
70
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Transverse Section
Detail of the transverse section of the 4" pipe 180° from the seam weld. The thickness of the pipe is 8 mm. No evidences of general corrosion or pitting were identified.
64
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Transverse Section
Aspect of the internal surface of the pipe after cleaning, showing the leakage line.
67
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Internal Surface

+2 more from this case →

ML00165 — SCC of Aluminum Bronze Heating CoilM - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Aspect of the external tube surface after cleaning. It is possible to see that the cracks are longitudinal to the tube and localized in positions where the surface is corroded.
132
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Surface AspectDf - External Surface
Aspect of the internal tube surface after a longitudinal cut, without cleaning. It is possible to see a clean surface inside the tube.
104
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Surface AspectDf - Internal Surface
Micrography of the external side of the bent tube, showing detachement of several grains due to intergranular corrosion. The corroded layer is about 200 microns thick at this position. The differences of colours in the corroded layer suggests a dealloying effect, also known as selective leaching.
71
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - External Surface
Micrography of a tube transverse section, at the through wall cracking position, showing intergranular morphology of the stress corrosion cracking. In the center of the thickness, far from the external surface corroded layer, the cracks are intergranular but did not present any dealloying evidence.
49
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - In the Center of the Thickness
SCC of Aluminum Bronze Heating Coil
1
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - General View

+2 more from this case →