Corrosion

4 cases · 12 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Replication Technique Detail focus: Microstructure clear all

Corrosion — sub-branches

Brittle Behavior 7Corrosion Fatigue 7Crevice 1Erosion Corrosion 1General Corrosion 1Intergranular Corrosion 3Localized Dissolution 2Pitting Corrosion 4Preferential Dissolution 4Stress Corrosion 9

Results

SortNewestOldestTitle A-ZTitle Z-A
Etched micrograph showing a transgranular crack running across equiaxed ferrite grains with dark grain-boundary carbides.
24
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - As polishedDf - Acicular Alpha
Teste João
2
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polishedDf - Acicular Alpha
Test
3
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Acicular Alpha
The forged valve presented an uniform tempered martensitic structure, surface hardness 246HB. Replication technique.
42
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - Kalling etched, OMDf - Martensite

More from these cases

ML00169 — Drill Pipe Fracture in the Pipe BodyM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Teste Joao
3
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polishedDf - Acicular Alpha
ML00155 — Failure of a Prestressed Concrete Steel StrandM - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
fadf asdf asdf
4
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Aligned particles
fasdf asfa sd
5
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Nital etched, OMDf - Austenite
fad asdf a
3
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Kalling etched, OMDf - Aligned particles
fasdfa fasdfasdf
3
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Acicular Ferrite
Test...
4
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Acicular Alpha

+1 more from this case →

ML00092 — MIC of a Valve BodyM - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Micrographic detail of the martensitic structure, hardness level about 246HB. Replication technique.
40
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - Kalling etched, OMDf - Martensite