Testpiece aspect

3 cases · 10 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: UNS clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification view of the broken tensile specimen fracture surface. The same macroscopic aspect as the WHEEL 1 fracture surface.
48
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Testpiece aspectDf - Ductile Fracture
Aspect of the broken tensile testpiece, cylindrical, in a longitudinal direction in the tubular casting, showing zero elongation and zero area reduction. The Yield Strenght (348MPa) is very close to the Ultimate Strenght (352MPa) in the tensile test. Yield to Ultimate ratio of 0.98.
28
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Testpiece aspectDf - Broken Testpiece
The spring fracture was rusted and did not allow the fractographic analysis. The quasecleavage and intergranular fracture micromechanisms presented in this scanning electron microscopy image were obtained from the Charpy V broken testpiece that presented 15J of absorbed energy at room temperature (21°C).
22
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Testpiece aspectDf - Brittle Fracture

More from these cases

ML00183 — Ductile Behavior of an Aluminum WheelM - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Detail of the broken tensile specimen fracture surface. Predominantly dimples.
45
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Testpiece aspectDf - Dimples
Tensile specimen fracture surface showing a small shrinkage and dimples, exactly as the WHEEL 1 fracture appearance (figure 7).
36
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Testpiece aspectDf - Fracture
In the broken specimen fracture surface there are also regions of small cracks, that appear secondary, but that did not propagate. The predominantly mechanism is dimples.
37
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Testpiece aspectDf - Cracks
Detail of the small cracks in a brittle phase, analyzed by EDS as rich in iron.
38
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Testpiece aspectDf - Brittle Cracks
Ductile Behavior of an Aluminum Wheel
2
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Testpiece aspectDf - Fracture

+1 more from this case →

ML00173 — Welding Cracks in an Aged HP Cast FittingM - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Welding Cracks in an Aged HP Cast Fitting
3
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Testpiece aspectDf - Broken Testpiece