Surface Aspect

2 cases · 3 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Finished Product Application: Ship Detail focus: Sampling and Analysis clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Detail of the external surface of the sleeve where the surface coating was detached, creating a lack of sealing condition.
67
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Surface AspectDf - External Surface
The macrography of the surface exposed to the combustion chamber presents multiple cracks, perpendicular to the internal diamater of the tube (left side of the figure). The cracks are located in the tube and propagated into the tube wall and welded joint to the plate (right side of the figure).
79
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - Surface AspectDf - At the Surface

More from these cases

ML00147 — WC Layer Detached from a Cast Lean DuplexM - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Macroscopic aspect of the OD surface of the sleeve (top of the figure), and a macrography of a longitudinal section (bottom of the figure). In the right side of the figure it is possible to see that the lack of sealing is associated to the detachment of the thermal spray surface layer.
26
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Surface AspectDf - Longitudinal Section