Scanning Electron Microscope

2 cases · 3 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Multiple cracks clear all

Scanning Electron Microscope — sub-branches

Surface Aspect by SEM 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Detail by scanning electron microscop of the clamp surface showing several cracks, parallel. In this image the cracks appear horizontal, but the photo was taken with the axis of the clamp in the vertical direction which means that the cracks are transverse to the axis.
41
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Surface Aspect by SEMDf - Multiple cracks
Microscopic detail of the cracks at the surface of the pin, close to the fracture. It is possible to see that the cracks are not associated to plastic deformation at the surface. Instead they are brittle and associated to regions where the material lost the passivation (dark grey stains at the surface). Some cracks that already opened (a little) showed deformation at the tips.
1024
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Surface Aspect by SEMDf - Multiple cracks

More from these cases

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Detailed aspect of the previous figure showing the parallel cracks, transverse to the axis.
37
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Surface Aspect by SEMDf - Multiple cracks