Scanning Electron Microscope

2 cases · 12 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Microstructure: Columnar Grains clear all

Scanning Electron Microscope — sub-branches

Nital Etched Micrography by SEM 12

Results

SortNewestOldestTitle A-ZTitle Z-A
Fusion line at the forging side. The weld metal to the top and the heat affected zone to the bottom.
84
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Fusion Line
Micrographic detail, by scanning electron micrography, of the pitting corrosion generating cracks, typical of a corrosion fatigue mechanism.
156
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by SEMDf - Pitting

More from these cases

ML00178 — Cold cracks in Cr-Mo Welded ForgingM - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Quenched and tempered heat affected zone of the forging.
75
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Heat Affected Zone
The cracking is located at the margin of the weld in the forging side. It is 1.2 mm deep.
66
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Cracking
The intergranular morphology of the cracks, at the heat affected zone of the forging, indicates it is a cold cracking probably formed when the welded joint was not yet post welding heat treated. The actual hardness values at the HAZ is 270HV10, and when it was cracked it was probably a lot higher.
71
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Intergranular Cracking
Detail of the cold cracking at the previous austenite grain boundary of the martensitic structure.
62
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Cold cracking
Detail of the cold cracking at the previous austenite grain boundary of the martensitic structure.
55
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Intergranular Cracking

+3 more from this case →

ML00163 — Corrosion Fatigue of a Boiler Waterwall TubeM - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Micrographic detail, by scanning electron microscopy, of the external tube surface, presenting the crack at the weld margin. The microstructure if ferritic in the left side (weld metal) and bainitic in the right side of the crack (heat affected zone).
90
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by SEMDf - Cracking
Corrosion Fatigue of a Boiler Waterwall Tube
4
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by SEMDf - Pearlite