Surface Aspect by SEM

2 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: S42000 clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Microscopic image by scanning electron microscope (SEM) of the ring surface that presented pites under fouling deposits.
522
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Pitting
Aspect of the rusted surface after cleaning, showing adhered products at the surface, in regions where the passive layer was destroyed and pitting corrosion occurred.
184
VIEW
ML00054 / Dec.2018
Cutlery Corrosion
M - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Corrosion

More from these cases

ML00124 — MIC of a Martensitic Valve RingM - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Microscopic details of the ring surface showing the fouling at the surface and localized corrosion under the deposits.
42
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Pitting
Higher magnification of the localized corrosion, showing that there are cracks at the margin of the corroded region.
39
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Pitting
SEM image showing a branching surface crack extending from a region of granular corrosion deposits into the polished substrate.
32
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Pitting
Intergranular morphology inside the pitting and evidences of chemical attack (dissolution).
36
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Pitting
ML00054 — Cutlery CorrosionM - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Detail of the rusted surface. EDS analysis inside the pitting shows a high Cl peak (the bright aspect inside the pitting), indicating that the salt over the surface was responsible for destroying the passive layer and the localized corrosion occurred.
172
VIEW
ML00054 / Dec.2018
Cutlery Corrosion
M - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Corrosion