Optical Microscope

37 cases · 227 images for “fracture”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Optical Microscope — sub-branches

As polished micrography 28Kalling Etched Micrography by OM 64Keller Etched Micrography by OM 2Micro by OM, picric acid+FeCl3+H2O etch 3Micrography by OM 1Micrography by OM using A262 Method A 2Micrography by OM, HF + HNO3 + H2O etch 1NaOH Electrolytic Etched Micro 14Nital Etched Micrography by OM 110Oxalic Acid Electrolytic Etch 2

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
The cast iron microstructure is predominatly ferritic with graphite nodules.
169
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Graphite in Nodules
Micrographic detail of the secondary crack from the fracture surface of the WHEEL 1, following the interdendritic precipitates.
36
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Keller Etched Micrography by OMDf - Fracture
The main crack is to the top and the blade surface is to the right, in this micrography that does not reveal any plastic deformation, with transgranular and integranular cracks.
24
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Brittle Fracture
Micrography of a longitudinal section of the flared tubing where the fracture occurred. The starting point of the fracture is associated to the external side of the tubing, where it was connected by a nut and there was a localized plastic deformation due to the fitting assembly.
33
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - Transgranular Fracture
SAMPLE 1 AT THE FRACTURE - Micrographic detail of the intergranular fracture. The austenitic grains of the material are loosing.
80
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Intergranular Fracture
Micrography of a longitudinal section of the pipe at the fracture position, in the thinner thickness. The diagonal line in the middle of the figure is the fracture surface and it is possible to identify that it was sheared with strong plastic deformation. The segregation bands (longitudinal lines) are deformed in the direction of the failure shearing, in a depth that is several milimeters deep in the pipe, from the fracture surface.
17
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - Nital Etched Micrography by OMDf - Ductile Fracture
Micrography of a typical overloaded wire, in a longitudinal section, showing plastic deformation and necking at the fracture. About 25% of the wires have ruptured by this ductile mechanism.
34
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Ductile Fracture
Micrographic detail of the final fracture by overloading after the fatigue crack propagated almost through the wall thickness. The microstructure presents strong plastic deformation around the crack, in a ferritic pearlitic structure.
29
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Nital Etched Micrography by OMDf - Ductile Fracture

More from these cases

ML00040 — Brittle Fracture of a Valve StemM - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
The micrography of the stem at the fracture region shows a flat fracture with transgranular clevage at the ferritic structure.
137
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
Micrography presenting a detail of the fracture surface opening to the graphite nodules.
139
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
ML00160 — High Temperature Degradation of 310SSM - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
SAMPLE 1, AT THE FRACTURE - Micrography, as polished, of the oxides at the fracture (zero thickness). In this region the oxide layer penetrated through thickness, intergranular, and fractured the material.
63
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - Intergranular Fracture
ML00155 — Failure of a Prestressed Concrete Steel StrandM - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Micrography of a typical as polished overloaded wire, in a longitudinal section, showing necking at the fracture and secondary ductile cracks. About 25% of the wires have ruptured by this ductile mechanism.
35
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polished micrographyDf - Ductile Fracture