Optical Microscope

34 cases · 338 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Tempered Martensite clear all

Optical Microscope — sub-branches

As polished micrography 41Eletrolytically Etched Micrography by OM 6Kalling Etched Micrography by OM 46Micro by OM, picric acid+FeCl3+H2O etch 3Micrography by OM 10Nital Etched Micrography by OM 232

Results

SortNewestOldestTitle A-ZTitle Z-A
The micrography in the longitudinal section in the middle of the thickness shows a light banding. Quenched and tempered structure.
346
VIEW
ML00037 / Jun.2017
LAS Forging for Pump Body
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrography of a longitudinal section of the bolt at the fracture surface. The material showed several creep voids and interconnected cracks. The broken bolt remained in service during some time and the fracture surface presented a thick oxide layer(grey). As polished.
529
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Micrography by OMDf - Oxide Layer

More from these cases

ML00037 — LAS Forging for Pump BodyM - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Typical manufacturing
Quenched and tempered structure of the 1" thick forging presenting a light banding.
43
VIEW
ML00037 / Jun.2017
LAS Forging for Pump Body
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Banded Structure
Longitudinal section in the middle of the thickness. Quenched and tempered structure.
38
VIEW
ML00037 / Jun.2017
LAS Forging for Pump Body
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Martensite
Vickers microhardness in and out of the segregation bands. The average hardness value in the band (1, 2 and 3 identations) is 354 HV 50g and out of the band (4, 5 and 6 identations) is 286 HV 50g.
33
VIEW
ML00037 / Jun.2017
LAS Forging for Pump Body
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Banded Structure
ML00004 — Creep in High Temperature BoltsM - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Micrographic detail of the creep voids and interconnected cracks. The broken bolt remained in service during some time and the fracture surface presented a thick oxide layer(grey). As polished.
121
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Micrography by OMDf - Interconnected Cracks
Micrographic detail of the creep voids and interconnected cracks. The broken bolt remained in service during some time and the fracture surface presented a thick oxide layer(grey). As polished.
101
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Micrography by OMDf - Voids
Micrography of a longitudinal section of a CrMov steel bolt that broke in service by a creep mechanism in a gas turbine. Tempered structure. Interconnected cracks paralled to the fracture surface.
95
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Nital Etched Micrography by OMDf - Crack
Micrographic detail of a longitudinal section of the bolt far from the fracture, presenting a tempered structure.
82
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Nital Etched Micrography by OMDf - Tempered Structure
Micrographic detail of a longitudinal section of the bolt close to the fracture, presenting an overtempered structure.
76
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Nital Etched Micrography by OMDf - Overtempered Structure