Optical Microscope

4 cases · 21 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Secondary carbides Detail focus: Sampling and Analysis clear all

Optical Microscope — sub-branches

As polished micrography 9Glyceregia Etched Micrography by OM 2Kalling Etched Micrography by OM 2Micrography by OM 3NaOH Electrolytic Etched Micro 2Oxalic Acid Electrolytic Etch 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Aged microstructure of the HP stainless steel, modified with 1%Nb, cast fitting, tubular, operating for 6 years in a furnace which design temperature is 1100°C. The material presented a network of primary carbides, white and grey, and an austenitic matrix with coalescing secondary precipitation. Some voids. The Vickers identation indicates a hardness value about 260HV 100g in the aged austenitic matrix.
491
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Microhardness identations
SAMPLE 1 AT THE FRACTURE - Micrography in low magnification where the thickness is reduced to zero (fracture). Side A (process side) to the bottom and side B (furnace environment side) to the top.
85
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Low Mag
Micrography close to the external surface of a new tube, sound.
48
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the External Surface
Micrography of the transverse section of the NEW TUBE, close to the external surface, showing the austenitic structure with primary carbides network.
59
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Close to the External Surface

More from these cases

ML00173 — Welding Cracks in an Aged HP Cast FittingM - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cast fitting microstructure. Network of primary carbides and austenitic matrix with coalescing secondary precipitation.
37
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Base Metal
As polished micrography of the fusion line presenting several microcracks . The base metal is to the top and the weld metal is to the bottom.
23
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - As polished micrographyDf - Fusion Line
ML00160 — High Temperature Degradation of 310SSM - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
SAMPLE 1 AT 1 mm THICKNESS - Micrography in low magnification in the center of the thickness. The microstructure is austenitic with secondary intergranular and intragranular precipitation.
77
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Low Mag
SAMPLE 2 AT 2 mm THICKNESS - Micrography in low magnification in the center of the thickness. The microstructure is austenitic with secondary intergranular and intragranular precipitation. No variation in the microstructure of the center of the plate, compared to sample 1.
52
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Low Mag
SAMPLE 3 AT 4 mm THICKNESS - Micrography in low magnification in the center of the thickness. The microstructure is austenitic with secondary intergranular and intragranular precipitation, but this micrography was obtained in the longitudinal section, presenting the plate alignment and was etched with NaOH, adopted to colour the sigma phase .
40
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - NaOH Electrolytic Etched MicroDf - Low Mag
SAMPLE 1 AT 1 mm THICKNESS - Micrography in low magnification in the center of the thickness, as polished. There are no regions of internal damage (like internal voids or cracks), indicating that the mechanism is only related to surface effects.
42
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - In the Center of the Thickness
SAMPLE 3, CLOSE TO THE SURFACE OF SIDE A - Micrography, as polished, of the oxides at the process side. In this region there is an oxide layer, not continuous but with no localized penetrations.
43
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - At the Surface

+3 more from this case →

ML00097 — Cast SS Tube Removed From High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Micrography close to the internal surface of a new tube, presenting casting defects.
47
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the Internal Surface
Micrography close to the internal surface of the tube removed from service after 6 month, presenting high temperature oxidation and shrinkage voids (casting defects).
31
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the Internal Surface
Micrography close to the external surface of the tube removed from service, damaged by high temperature oxidation.
25
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - As polished micrographyDf - Close to the External Surface
ML00038 — Cast SS Tube for High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
The micrography in the as polished condition of the NEW TUBE shows that there are no casting defects close to the external surface.
49
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Close to the External Surface
The micrography in the as polished condition of the NEW TUBE shows that there are no casting defects in the center of the thickness.
47
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Transverse Section
Micrography of the transverse section of the TUBE REMOVED FROM SERVICE,close to the external surface, showing the austenitic structure with coalesced carbides and secondary precipitation.
39
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Close to the External Surface
The micrography in the as polished condition of the TUBE REMOVED FROM SERVICE shows that after one year operating in high temperature the material opens voids in the center of the thickness. Even the secondary carbide is coalesced.
36
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Transverse Section